Influence of Heat Treatment on Corrosion Resistance of High-Velocity Oxygen-Fuel Sprayed WC-17Co Coatings on 42CrMo Steel

The influence of heat treatment from 500 to 1100 A degrees C on the 5 wt.% H2SO4 solution-induced corrosion resistance of high-velocity oxygen-fuel sprayed WC-17Co coatings on 42CrMo steel was investigated, by using x-ray diffractometer (XRD), scanning electron microscopy (SEM)-energy-dispersive spectrometer (EDS), and polarization curve methods. XRD analysis showed decrease in W2C phase intensity with recrystallization of amorphous Co and generation of new Co3W3C and Co6W6C phases with heat treatment. Porosity distribution did not follow a particular pattern; it initially increased and then decreased with increasing temperature. Corrosion resistance sequence of the as-sprayed and heat-treated coatings in 5 wt.% H2SO4 solution was C-5 > C-9 > C-A > C-7 > C-11. Furthermore, microstructure and phase structure of heat-treated coatings revealed the formation of different discontinuous plate-like oxide films on the surface of the heat-treated coatings which indicated the vital effect of binder structure on the corrosion resistance.