Development of an electrochemical sensor based on nanostructured hausmannite-type manganese oxide for detection of sodium ions

The preparation and electrochemical characterization of hausmannite-type manganese oxide to use as a sensing material for sodium ion is described. This paper reports a new via synthetic to obtain of the hausmannite-type manganese oxide and its application in the construction of modified electrode as a voltammetric sensor. The electrochemical activity of hausmannite-type manganese oxide is controlled by intercalation/deintercalation of the sodium ions within the oxide lattice. The detection is based on the measurement of anodic current generated by oxidation of Mn-III-Mn-IV at electrode surface. The best electrochemical response was obtained for a sensor composition of 20% (w/w) hausmannite oxide in the paste, a TRIS buffer solution of pH 6.0-7.0 and a scan rate of 50 mV s(-1). A sensitive linear voltammetric response for sodium ions was obtained in the concentration range of 2.01 x 10(-5)-2.09 x 10(-4) mol L-1 with a slope of 355 mu A L mmol(-1) and a detection limit of 7.50 x 10(-6) mol L-1 using cyclic voltammetry. The use of hausmannite has significantly improved the selectivity of the sensor compared to the birnessite-type manganese oxide modified electrode. Under the working conditions, the proposed method was successfully applied to determination of sodium ions in urine samples. (c) 2013 Elsevier B.V. All rights reserved.