Preparation of Mg2FeH6 Nanoparticles for Hydrogen Storage Properties

被引：10

作者：

Niaz, N. A. ^{[1
]}

Ahmad, I. ^{[2
]}

Khalid, N. R. ^{[1
]}

Ahmed, E. ^{[1
]}

Abbas, S. M. ^{[3
]}

Jabeen, N. ^{[3
]}

机构：

[1] Bahauddin Zakariya Univ, Dept Phys, Multan 60800, Pakistan

[2] COMSATS Inst Informat Technol, Islamabad 44000, Pakistan

[3] Natl Ctr Phys, Islamabad 44000, Pakistan

来源：

JOURNAL OF NANOMATERIALS | 2013年 / 2013卷

关键词：

MG-FE-H; MAGNESIUM; TRANSITION; NI; HYDRIDES; SORPTION; ALLOY; MECHANISM; BEHAVIOR; MG2COH5;

D O I：

10.1155/2013/610642

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Magnesium (Mg) and iron (Fe) nanoparticles are prepared by thermal decomposition of bipyridyl complexes of metals. These prepared Mg-Fe (2 : 1) nanoparticles are hydrogenated under 4 MPa hydrogen pressure and 673 K for 48 hours to achieve Mg2FeH6. Their structural analysis was assessed by applying manifold techniques. The hydrogen storage properties of prepared compound were measured by Sieverts type apparatus. The desorption kinetics were measured by high pressure thermal desorption spectrometer (HP-TDS). More than 5 wt% hydrogen released was obtained by the Mg2FeH6 within 5 min, and during rehydrogenation very effective hydrogen absorption rate was observed by the compound.

引用

收藏

页数：7

相关论文

共 36 条

[1] ENVIRONMENTAL-DAMAGE DUE TO FOSSIL-FUELS USE [J].

BARBIR, F ;

VEZIROGLU, TN ;

PLASS, HJ .

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1990, 15 (10) :739-749

[2] Catalytic mechanism of transition-metal compounds on Mg hydrogen sorption reaction [J].

Barkhordarian, Gagik ;

Klassen, Thomas ;

Bormann, Rudiger .

JOURNAL OF PHYSICAL CHEMISTRY B, 2006, 110 (22) :11020-11024

[3] Addition of nanosized Cr2O3 to magnesium for improvement of the hydrogen sorption properties [J].

Bobet, JL ;

Desmoulins-Krawiec, S ;

Grigorova, E ;

Cansell, F ;

Chevalier, B .

JOURNAL OF ALLOYS AND COMPOUNDS, 2003, 351 (1-2) :217-221

[4] Hydrogenation of transition element additives (Ti, V) during ball milling of magnesium hydride [J].

Charbonnier, J ;

de Rango, P ;

Fruchart, D ;

Miraglia, S ;

Pontonnier, L ;

Rivoirard, S ;

Skryabina, N ;

Vulliet, P .

JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 383 (1-2) :205-208

[5]

Didishein J.-J., 1984, INORG CHEM, V23, P1953

[6] Hydrogen storage in magnesium-based hydrides and hydride composites [J].

Dornheim, M. ;

Doppiu, S. ;

Barkhordarian, G. ;

Boesenberg, U. ;

Klassen, T. ;

Gutfleisch, O. ;

Bormann, R. .

SCRIPTA MATERIALIA, 2007, 56 (10) :841-846

[7] Synthesis of Mg2FeH6 by reactive mechanical alloying:: formation and decomposition properties [J].

Gennari, FC ;

Castro, FJ ;

Gamboa, JJA .

JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 339 (1-2) :261-267

[8] Hydrogen desorption behavior from magnesium hydrides synthesized by reactive mechanical alloying [J].

Gennari, FC ;

Castro, FJ ;

Urretavizcaya, G .

JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 321 (01) :46-53

[9] Catalytic effect of nanoparticle 3d-transition metals on hydrogen storage properties in magnesium hydride MgH2 prepared by mechanical milling [J].

Hanada, N ;

Ichikawa, T ;

Fujii, H .

JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (15) :7188-7194

[10] Preparation of the hydrides Mg2FeH6 and Mg2CoH5 by mechanical alloying followed by sintering [J].

Huot, J ;

Hayakawa, H ;

Akiba, E .

JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 248 (1-2) :164-167

← 1 2 3 4 →