Crystallization mechanism and corrosion property of electroless nickel phosphorus coating during intermediate temperature oxidation

被引：54
作者：
Sribalaji, M. [1 ]
Arunkumar, P. [2 ]
Babu, K. Suresh [2 ]
Keshri, Anup Kumar [1 ]
机构：
[1] Indian Inst Technol Patna, Mat Sci & Engn, Patna 800013, Bihar, India
[2] Pondicherry Univ, Madanjeet Sch Green Energy Technol, Ctr Nanosci & Technol, Pondicherry 605014, India
来源：
APPLIED SURFACE SCIENCE | 2015年 / 355卷
关键词：
Electroless; Ni-P coating; Oxidation; Crystallization; Corrosion; NI-P; HEAT-TREATMENT; GRAIN-SIZE; RESISTANCE; BEHAVIOR; WEAR; STEEL;
D O I：
10.1016/j.apsusc.2015.07.061
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Electroless Ni-P coating was deposited on steel substrate and the effect of intermediate temperature oxidation on crystallization mechanism and corrosion properties of the coating was investigated. Ni-P coatings were annealed at three different temperatures, viz. 200 degrees C, 400 degrees C and 600 degrees C for 2 h in air. Formation of nickel oxide (NiO) was observed in the coating upon annealing beyond the crystallization temperature (330 degrees C). Crystallization mechanism provided insight about the step by step formation of long range ordered Ni,Ni3P and NiO phases.Improvement in the corrosion resistance of Ni-P coating compared to bare steel was found to be similar to 21% on annealing at 400 degrees C in air which gradually increased to similar to 31% on annealing the coating at 600 degrees C in air. Increasedcorrosion resistance at 400 degrees C annealed, coating was attributed to the formation of crystalline Ni and Ni3P phases. Two simultaneously effects hive identified for the increased corrosion resistance of the coating annealed at 600 degrees C in air. (a) Formation of NiO layer which acts as a passivation layer and protects the underlying P enriched layer and (b) absence of an interdiffusion layer from substrate to coating. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：112 / 120
页数：9
相关论文
共 26 条
[1]   The corrosion behavior of Ni-P deposits with high phosphorous contents in brine media [J].
Bai, A ;
Chuang, PY ;
Hu, CC .
MATERIALS CHEMISTRY AND PHYSICS, 2003, 82 (01) :93-100
[2]   Study of substrate temperature effects on structural, optical, mechanical and opto-thermal properties of NiO sprayed semiconductor thin films [J].
Boukhachem, A. ;
Boughalmi, R. ;
Karyaoui, M. ;
Mhamdi, A. ;
Chtourou, R. ;
Boubaker, K. ;
Amlouk, M. .
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2014, 188 :72-77
[3]   An efficient route to a porous NiO/reduced graphene oxide hybrid film with highly improved electrochromic properties [J].
Cai, Guo-fa ;
Tu, Jiang-ping ;
Zhang, Jun ;
Mai, Yong-jin ;
Lu, Yi ;
Gu, Chang-dong ;
Wang, Xiu-li .
NANOSCALE, 2012, 4 (18) :5724-5730
[4]   The corrosion resistance of electroless deposited nano-crystalline Ni-P alloys [J].
Crobu, Maura ;
Scorciapino, Andrea ;
Elsener, Bernhard ;
Rossi, Antonella .
ELECTROCHIMICA ACTA, 2008, 53 (08) :3364-3370
[5]   Oxidation behavior of electroless Ni-P, Ni-B and Ni-W-B coatings deposited on steel substrates [J].
Eraslan, Sinem ;
Urgen, Mustafa .
SURFACE & COATINGS TECHNOLOGY, 2015, 265 :46-52
[6]   Crystallization temperature of amorphous electroless nickel-phosphorus alloys [J].
Gao, JQ ;
Wu, YT ;
Lei, L ;
Bin, S ;
Hu, WB .
MATERIALS LETTERS, 2005, 59 (13) :1665-1669
[7]   CORRELATION BETWEEN STRESS VOIDING OF AL(SI)(CU) METALLIZATIONS AND CRYSTAL ORIENTATION OF ALUMINUM GRAINS [J].
KORDIC, S ;
WOLTERS, RAM ;
TROOST, KZ .
JOURNAL OF APPLIED PHYSICS, 1993, 74 (09) :5391-5394
[8]   Finite element analysis of the grain size effect on diffusion in polycrystalline materials [J].
Lacaille, V. ;
Morel, C. ;
Feulvarch, E. ;
Kermouche, G. ;
Bergheau, J. -M. .
COMPUTATIONAL MATERIALS SCIENCE, 2014, 95 :187-191
[9]   Structure, electrochemical and wear-corrosion properties of electroless nickel-phosphorus deposition on CFRP composites [J].
Lee, C. K. .
MATERIALS CHEMISTRY AND PHYSICS, 2009, 114 (01) :125-133
[10]  
Lin NM, 2015, INT J ELECTROCHEM SC, V10, P356
123