Direct fabrication of thin-film LiTi2(PO4)3 electrodes using the hydrothermal method

被引：5
作者：
Liang, Yanjie [1 ,2 ]
Hisamo, Taro [1 ]
Sumi, Suguru [1 ]
Kamiike, Yuichiro [1 ]
Kuroda, Kensuke [1 ]
Okido, Masazumi [1 ]
机构：
[1] Nagoya Univ, Inst Mat & Syst Sustainabil, Nagoya, Aichi, Japan
[2] Cent S Univ, Sch Met & Environm, Changsha, Hunan, Peoples R China
来源：
SOLID STATE IONICS | 2016年 / 296卷
关键词：
Hydrothermal method; Solid film electrode; LiTi2(PO4)(3); Ionic conductivity; LITHIUM TITANIUM PHOSPHATE; HIGH-RATE PERFORMANCE; LI-ION BATTERIES; ELECTROCHEMICAL PROPERTIES; SOLID ELECTROLYTES; ANODE MATERIAL; CONDUCTIVITY; LIFEPO4;
D O I：
10.1016/j.ssi.2016.08.006
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this study, the thin-film solid electrode LiTi2(PO4)(3) (LTP) was in-situ fabricated and sequentially deposited on a substrate using a hydrothermal method. The results suggest that crystals of the LTP film evolve from whisker clusters to cubes and that the crystalline region nucleates at the interface with the substrate and grows outwards. After a 48-hour reaction, the cubic-shaped LTP crystals formed a dense LTP film with few pores and peeling or flaking at the interface with the substrate. However, the cubic-shaped solid electrolyte is not favourable for charge transfer and Li+ ion diffusion, resulting in a poor ionic conductivity of approximately 1.0 x 10(-7) S/cm. Fortunately, the hydrothermal process offers a possible method for doping the Al3+ into the LTP film, and the ionic conductivity increases to as higher as 1.4 x 10(-3) S/cm as a result of the modified LW grain boundary. This study demonstrates that hydrothermal technology is a potential method for fabricating thin-film lithium battery materials. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：7 / 12
页数：6
相关论文
共 36 条
[21]   Hydrothermal Synthesis and Electrochemical Properties of Li3V2(PO4)3/C-Based Composites for Lithium-Ion Batteries [J].
Sun, Chunwen ;
Rajasekhara, Shreyas ;
Dong, Youzhong ;
Goodenough, John B. .
ACS APPLIED MATERIALS & INTERFACES, 2011, 3 (09) :3772-3776
[22]   Synthesis and Electrochemical Performance of a Lithium Titanium Phosphate Anode for Aqueous Lithium-Ion Batteries [J].
Wessells, Colin ;
La Mantia, Fabio ;
Deshazer, Heather ;
Huggins, Robert A. ;
Cui, Yi .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2011, 158 (03) :A352-A355
[23]   Electrical and mechanical properties of hot-pressed versus sintered LiTi2(PO4)3 [J].
Wolfenstine, J. ;
Allen, J. L. ;
Sumner, J. ;
Sakamoto, J. .
SOLID STATE IONICS, 2009, 180 (14-16) :961-967
[24]   Single-crystalline Li4Ti5O12 nanorods and their application in high rate capability Li4Ti5O12/LiMn2O4 full cells [J].
Xi, Liu Jiang ;
Wang, Hong Kang ;
Yang, Shi Liu ;
Ma, Ru Guang ;
Lu, Zhou Guang ;
Cao, Chen Wei ;
Leung, Kwan Lan ;
Deng, Jian Qiu ;
Rogach, Andrey L. ;
Chung, C. Y. .
JOURNAL OF POWER SOURCES, 2013, 242 :222-229
[25]  
Xiong L., 2015, J SOLID STATE ELECTR, V1
[26]   Hydrothermal Synthesis of Li4Ti5O12/TiO2 Nano-composite As High Performance Anode Material for Li-Ion Batteries [J].
Xu, Chao ;
Xue, Lihong ;
Zhang, Wen ;
Fan, Xin ;
Yan, Youwei ;
Li, Qiang ;
Huang, Yunhui ;
Zhang, Wuxing .
ELECTROCHIMICA ACTA, 2014, 147 :506-512
[27]   A review of processes and technologies for the recycling of lithium-ion secondary batteries [J].
Xu, Jinqiu ;
Thomas, H. R. ;
Francis, Rob W. ;
Lum, Ken R. ;
Wang, Jingwei ;
Liang, Bo .
JOURNAL OF POWER SOURCES, 2008, 177 (02) :512-527
[28]   Enhanced rate performance of Li4Ti5O12 anode material by ethanol-assisted hydrothermal synthesis for lithium-ion battery [J].
Yi, Ting-Feng ;
Yang, Shuang-Yuan ;
Zhu, Yan-Rong ;
Ye, Ming-Fu ;
Xie, Ying ;
Zhu, Rong-Sun .
CERAMICS INTERNATIONAL, 2014, 40 (07) :9853-9858
[29]  
Yong Y., 1990, J MATER SCI LETT, V9, P1392
[30]   Direct fabrication of thin-film LiNiO2 electrodes in LiOH solution by electrochemical-hydrothermal method [J].
Yoshimura, M ;
Han, KS ;
Tsurimoto, S .
SOLID STATE IONICS, 1998, 106 (1-2) :39-44
1234