Thermally induced structural and mechanical variations in ternary Al-Si based alloys

被引：8

作者：

Abd El-Salam, F. ^{[1
]}

Abd El-Khalek, A. M. ^{[1
]}

Nada, R. H. ^{[1
]}

Wahab, L. A. ^{[2
]}

Zahran, H. Y. ^{[1
]}

机构：

[1] Ain Shams Univ, Fac Educ, Dept Phys, Cairo, Egypt

[2] Natl Ctr Radiat Res & Technol, Nasr, Cairo, Egypt

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2009年 / 527卷 / 1-2期

关键词：

Al-Si based ternary alloys; Mechanical parameters; Homogenization; Peritectic structure; Reticulate phases; ALUMINUM-SILICON ALLOYS; EQUILIBRIUM RELATIONS; HIGH-PURITY; BEHAVIOR;

D O I：

10.1016/j.msea.2009.08.002

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of heat treatment on the variations in the structural and mechanical characteristics of Al-Si based ternary alloys was studied for samples prepared from elements of purity 99.99% and aged at 673 K for 2 h through tensile tests in the temperature range (413-493 K). Softening behaviour was observed with increasing the working temperature. The mechanical results were discussed in relation to the structure analysis of TEM micrographs obtained at room temperature for samples aged at 673 K. Sn addition improved the mechanical properties of the samples but this was not achieved with Ag addition which improved softening and ductility under the same testing conditions. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：281 / 286

页数：6

共 24 条

[11]

MURRAY JL, 1984, ASM HDB, V3, P52

[12] DENDRITIC STRUCTURE IN UNIDIRECTIONALLY SOLIDIFIED ALUMINUM, TIN, AND ZINC BASE BINARY-ALLOYS [J].

OKAMOTO, T ;

KISHITAKE, K .

JOURNAL OF CRYSTAL GROWTH, 1975, 29 (02) :137-146

[13] BEHAVIOR OF EXCESS VACANCIES DURING NUCLEATION OF PRECIPITATES IN ALUMINUM-SILICON ALLOYS [J].

OZAWA, E ;

KIMURA, H .

MATERIALS SCIENCE AND ENGINEERING, 1971, 8 (06) :327-&

[14]

RAJAB E, 1989, ACTA METALL, V38, P2709

[15]

Rajan T.V., 1995, Tribology Transactions, V36, P121

[16]

RAYNOR GV, 1949, PHILOS MAG, V40, P404

[17]

SALEM HAA, 1982, 2 CAIR U MDP C 27 29

[18]

SOTO Y, 1994, 940691 SAE, P454

[19]

SUERY M, 1980, PHILOS MAG A, V41, P41, DOI 10.1080/01418618008241830

[20]

SULLY AH, 1949, J I MET, V76, P269

← 1 2 3 →