Corrosion inhibition using 2-mercaptobenzimidazole on T6 treated 6061 Al-SiCp composite in acetic acid

被引：5
作者：
Chacko, Melby [1 ]
Nayak, Jagannath [1 ]
机构：
[1] NITK, Dept Met & Mat Engn, Mangaluru 575025, India
来源：
MATERIALS TODAY-PROCEEDINGS | 2015年 / 2卷 / 4-5期
关键词：
Al-SiCp composite; T6; treatment; corrosion; inhibition; chemisorption; MILD-STEEL; ALLOY; BEHAVIOR; DERIVATIVES; ADSORPTION; COPPER;
D O I：
10.1016/j.matpr.2015.07.257
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
6061 Al-SiCp composite was T6 treated by solutionizing the sample at 350 degrees C and water quenching. It was then underaged at 140 degrees C and aging profile was obtained using Rockwell B hardness. Corrosion characteristics of the underaged composite was studied at varying temperatures. Acetic acid in altered concentrations was used as medium for corrosion studies. 2-mercaptobenzimidazole was added in different concentrations for inhibiting the corrosion reaction. Inhibition efficiency and thermodynamic parameters supported that 2-mercaptobenzimidazole is an effective inhibitor which adsorbed on to the surface by mixed adsorption where chemisorption was predominant. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2728 / 2736
页数：9
相关论文
共 48 条
[11]   Corrosion inhibition of copper and aluminium by 2-mercaptobenzimidazole and octylphosphonic acid-Surface pre-treatment and method of film preparation [J].
Kozlica, Dzevad K. ;
Milosev, Ingrid .
ELECTROCHIMICA ACTA, 2022, 431
[12]   3-Ethyl-4-amino-5-mercapto-1,2,4-triazole as a Corrosion Inhibitor for 6061/Al-15 vol% SiCp Composite in a Sodium Hydroxide Solution [J].
Kumari, P. D. Reena ;
Nayak, Jagannath ;
Shetty, A. Nityananda .
SYNTHESIS AND REACTIVITY IN INORGANIC METAL-ORGANIC AND NANO-METAL CHEMISTRY, 2011, 41 (07) :774-784
[13]   Effect of a T6 aging treatment on the corrosion behaviour of in-situ AlxNiy reinforced AA6061 composite [J].
Vishwanatha, A. D. ;
Panda, Bijayani ;
Shivanna, D. M. .
MATERIALS TODAY-PROCEEDINGS, 2021, 44 :4112-4117
[14]   Application of QFA coupled with CFD analysis to predict the hardness of T6 heat treated Al6061 cylinder [J].
Ko, Dae-Hoon ;
Ko, Dae-Cheol ;
Lim, Hak-Jin ;
Kim, Byung-Min .
JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY, 2013, 27 (09) :2839-2844
[15]   Corrosion inhibition of 6061 Al-15 vol. pct. SiC(p) composite and its base alloy in a mixture of sulphuric acid and hydrochloric acid by 4-(N,N-dimethyl amino) benzaldehyde thiosemicarbazone [J].
Pinto, Geetha Mable ;
Nayak, Jagannath ;
Shetty, A. Nityananda .
MATERIALS CHEMISTRY AND PHYSICS, 2011, 125 (03) :628-640
[16]   Microstructure and Wear Properties of T6 Heat Treated Semisolid A356-TiB2 composite [J].
Zulkamal, N. A. M. ;
Nasir, L. M. M. ;
Anasyida, A. S. .
REGIONAL CONFERENCE ON MATERIALS AND ASEAN MICROSCOPY CONFERENCE 2017 (RCM & AMC 2017), 2018, 1082
[17]   Effect of magnesium ions on the protective power of corrosion products formed on the surface of Al 6061 T6 alloy 10% Al2O3 (v/v) composite in solutions containing chlorides [J].
Traverso, P ;
Beccaria, AM .
SURFACE AND INTERFACE ANALYSIS, 1998, 26 (07) :524-530
[18]   Estimation of fracture toughness (KIC) using Charpy impact test for Al6061T6 and Al7075T6 alloys subjected to corrosion [J].
Kumar, S. Sunil ;
Londe, Neelakantha, V ;
Kumar, K. Dilip ;
Kittur, Mohammed Ibrahim .
MATERIALS TODAY-PROCEEDINGS, 2021, 46 :2414-2420
[19]   Corrosion behavior of an artificially aged (T6) Al-Si-Mg-based metal matrix composite [J].
Dikici, B. ;
Gavgali, M. ;
Tekmen, C. .
JOURNAL OF COMPOSITE MATERIALS, 2006, 40 (14) :1259-1269
[20]   Mechanistic study of thin film sulfuric acid anodizing rate difference between Al2024 T3 and Al6061 T6 [J].
Ding, Zhongfen .
SURFACE & COATINGS TECHNOLOGY, 2019, 357 :280-288
12345