Chemical synthesis of aluminum nanoparticles

An alternate synthetic route has been described for the production of aluminum nanoparticles (Al-NPs). These Al-NPs were obtained through a reduction of aluminum acetylacetonate [Al(acac)(3)] by lithium aluminum hydride (LiAlH4) in mestitylene at 165 degrees C. The side products were removed by repeated washing with dry, ice cold methanol and the reaction mixture was filtered to obtain gray-colored Al-NPs. The synthesized nanoparticles were characterized by Powder X-ray diffraction pattern and Al-27-MAS-NMR spectrum. The X-ray diffraction pattern confirmed the formation of face-centered cubic (fcc) form of aluminum. The size and morphology were investigated by scanning electron microscope and transmission electron microscope which showed particle of varying shapes with size ranging from 50 to 250 nm. The weight loss from the nanoparticles was studied by thermo gravimetric analysis which indicated that the nanoparticles were tightly bound with an unknown amorphous organic residue which cannot be removed by simple washing. The carbonaceous residue might be outcome of the decomposition of acac ligand which was responsible in stabilizing aluminum nanoparticles.