Influence of hold period on creep-fatigue deformation behaviour of nickel base superalloy

被引:48
作者
Zrník, J [1 ]
Semenák, J [1 ]
Vrchovinsky, V [1 ]
Wangyao, P [1 ]
机构
[1] Tech Univ Kosice, Dept Mat Sci, Kosice 04001, Slovakia
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2001年 / 319卷
关键词
nickel base superalloy; low cycle fatigue; hold time; fatigue life; microstructure; damage;
D O I
10.1016/S0921-5093(01)01030-9
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The deformation behaviour and damage mechanisms of the wrought nickel base superalloy EI 698 VD has been investigated in condition of creep-fatigue loading. The alloy was subjected to load controlled isothermal low cycle fatigue at 650degreesC with superimposed hold periods of constant tensile load simulating creep stress component. The introduced hold periods were in range of 3 min to 10 h. The pure fatigue and pure creep tests were conducted as well. The test were of tension-tension type defined by stress ratio R = 0.027. During hold periods a constant stress of sigma = 740 MPa was maintained leading to pure creep. The tests were conducted until fracture. The influence of hold time was evaluated through the deformation behaviour. fatigue life, and fracture mechanisms participating in failure process. The time to fracture decreased continuously with increasing hold period. Considering the fatigue life achieved after shortening the hold time to 1 min, the life time measured was more than 10 times higher than in case of pure creep. The strain rate dependence achieved within this testing showed inverse dependence with respect to the hold time, The microstructure examination of the fractured specimens, using transmission electron microscopy (TEM), enabled to reveal the participating dislocation mechanisms for combined loading. The fracture analysis of broken up specimens showed that fatigue mechanisms became active at crack nucleation sites and crack propagation in time of testing when hold time was 30 min and less. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:637 / 642
页数:6
相关论文
共 13 条
  • [1] ANTALOVICH CD, 1981, MET T A, V12, P473
  • [2] BOSIMER DA, 1990, T ASME, V112, P68
  • [3] CHATEAU E, 1998, P 6 LIEG C MAT ADV P, P1197
  • [4] CHEN W, 1998, P 6 LIEG C MAT ADV P, P1069
  • [5] Day M. F., 1979, Metal Science, V13, P25, DOI 10.1179/030634579790434132
  • [6] THE HIGH-TEMPERATURE DEFORMATION IN CYCLIC LOADING OF A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY
    GABB, TP
    WELSCH, G
    [J]. ACTA METALLURGICA, 1989, 37 (09): : 2507 - 2516
  • [7] HARKEGARD G., 1998, P 6 LIEG C MAT ADV P, P913
  • [8] LEVEILLANT C, 1977, MECH BEHAV MAT, P163
  • [9] CYCLIC CREEP AND STRESS RUPTURE OF A MECHANICALLY ALLOYED OXIDE DISPERSION AND PRECIPITATION STRENGTHENED NICKEL-BASE SUPER-ALLOY
    NARDONE, VC
    MATEJCZYK, DE
    TIEN, JK
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (07): : 1435 - 1441
  • [10] Portella P.D., 1996, FATIGUE 96, P795