Influence of Cr on the oxidation of Fe3Al and Ni3Al at 500°C

被引：17

作者：

Velon, A ^{[1
]}

Yi, DQ ^{[1
]}

机构：

[1] Chalmers Univ Technol, Dept Engn Met, S-41296 Gothenburg, Sweden

来源：

OXIDATION OF METALS | 2002年 / 57卷 / 1-2期

关键词：

aluminides; Ni3Al; Fe3Al; dry air; Cr; high-temperature oxidation;

D O I：

10.1023/A:1013386427567

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The influence of chromium on the mechanical properties of the aluminides Fe3Al and Ni3Al has been studied extensively. In order to evaluate the role of Cr during the early stages of oxidation, Fe3Al and Ni3Al containing 2 and 4 at.% Cr were oxidized in dry air at 500degreesC for 6, 50, and 100 hr. The oxide scale on Fe3Al consists of a layer of Fe2O3 mixed with FeAl2O4 on top of a continuous layer of (Al, Cr)(2)O-3. Ni3Al is covered with a mixed layer of (Al, Cr)(2)O-3 and NiO/NiAl2O4 underneath a layer of NiO/NiAl2O4. Moreover, Cr induces the nucleation and growth of Fe2O3 and NiO particles at the oxide surface of Fe3Al and Ni3Al, respectively. This is due to enhanced cationic diffusion through the Cr-modified oxides. As a conclusion, additions of Cr zip to 4 at.% are detrimental to the oxidation behavior of both aluminides at 500degreesC.

引用

页码：13 / 31

页数：19

共 29 条

[11]

KOFSTAD P, 1988, HIGH TEMPERATURE COR, P92

[12]

KUBASCHEWSKI O, 1967, OXIDATION METALS ALL, V1

[13] NICKEL ALUMINIDES FOR STRUCTURAL USE [J].

LIU, CT ;

SIKKA, VK .

JOURNAL OF METALS, 1986, 38 (05) :19-21

[14]

LIU CT, 1990, METALS HDB, V2, P913

[15]

LIU CT, 1998, INTERMETALLIC COMPOU, V2, P17

[16] EFFECT OF CHROMIUM ON ROOM-TEMPERATURE DUCTILITY AND FRACTURE MODE IN FE3AL [J].

MCKAMEY, CG ;

HORTON, JA ;

LIU, CT .

SCRIPTA METALLURGICA, 1988, 22 (10) :1679-1681

[17]

OLEFJORD I, 1995, P EUR C APPL SURF IN, P155

[18] LONG-TERM OXIDATION BEHAVIOR OF NI3AL ALLOYS WITH AND WITHOUT CHROMIUM ADDITIONS [J].

PAN, YC ;

CHUANG, TH ;

YAO, YD .

JOURNAL OF MATERIALS SCIENCE, 1991, 26 (22) :6097-6103

[19] SUB-SOLIDUS PHASE EQUILIBRIA IN AL2O3-CR2O3 [J].

ROY, DM ;

BARKS, RE .

NATURE-PHYSICAL SCIENCE, 1972, 235 (58) :118-&

[20] OXIDATION BEHAVIOR OF NI3AL-0.1B CONTAINING 2CR [J].

TANIGUCHI, S ;

SHIBATA, T .

OXIDATION OF METALS, 1987, 28 (3-4) :155-163

← 1 2 3 →