Microstructural, mechanical and weldability assessments of the dissimilar welds between γ′- and γ"-strengthened nickel-base superalloys

Dissimilar welding of gamma'- and gamma ''-strengthened nickel-base superalloys has been investigated to identify the relationship between the microstructure of the welds and the resultant mechanical and weldability characteristics. gamma'-Strengthened nickel-base Alloy 500 and gamma ''-strengthened nickel-base Alloy 718 were used for dissimilar welding. Gas tungsten arc welding operations were utilized for performing the autogenous dissimilar welding. Alloy 500 and Alloy 718 base metals showed various types of phases, carbides, intermetallics and eutectics in their microstructure. The results for Alloy 500 weld metal showed severe segregation of titanium to the interdendritic regions. The Alloy 718 weld metal compositional analysis confirmed the substantial role of Nb in the formation of low-melting eutectic-type morphologies which can reduce the weldability. The microstructure of dissimilar weld metal with dilution level of 65% wt.% displayed semi-developed dendritic structure. The less segregation and less formation of low-melting eutectic structures caused to less susceptibility of the dissimilar weld metal to the solidification cracking. This result was confirmed by analytic modeling achievements. Dissolution of gamma ''-Ni3Nb precipitations took place in the Alloy 718 heat-affected zone leading to sharp decline of the microhardness in this region. Remelted and resolidified regions were observed in the partially-melted zone of Alloy 500 and Alloy 718. Nevertheless, no solidification and Equation cracking happened in the dissimilar welds. Finally, this was concluded that dissimilar welding of gamma'- and gamma ''-strengthened nickel-base superalloys can successfully be performed. (C) 2013 Elsevier Inc. All rights reserved.