Stabilization of α-BiFeO3 structure by Sr2+ and its effect on multiferroic properties

We report a study on the effect of the substitution of Bi3+ by Sr2+ on the stabilization of R3c structure of Bi1-xSrxFeO3 (0 <= x <= 0.3, Delta x = 0.05), and its effect in the magnetic and dielectric behavior. Stoichiometric mixtures of Bi2O3, Fe2O3 and SrO were mixed and milled for 5 h using a ball to powder weight ratio of 10:1 by high-energy ball milling. The obtained powder were pressed at 900 MPa to obtain cylindrical pellets and sintered at 800 degrees C for 2 h. X-ray diffraction and Rietveld refinement were used to evaluate the effect of Sr2+ on the crystal structure. In addition, vibrating sample magnetometry (VSM) and dielectric tests were used for describing the multiferroic behavior, The results show that Sr-doped BiFeO3 particles present rhombohedral structure (R3c) characteristic of alpha-BiFeO3 when the doping is below 0.10 mol of Sr. Additionally, a gradual decrease in the amount of secondary phases with the increase of the amount of strontium is observed. For doping concentration higher than 0.15 mol of Sr, a phase transition to an orthorhombic symmetry (beta-BiFeO3, Pbnm) is detected. Besides, changes in relative intensities of reflection peaks planes (110) and (104) are associated with the phase transformations and with the magnetic and dielectric behavior. The alpha-BiFeO3 phase show antiferromagnetic behavior and high values of dielectric permittivity, whereas the beta-BiFeO3 phase show a ferromagnetic behavior and low dielectric permittivity.