Effects of Sintering Temperature on Properties of W-9.8Ni-4.2Fe Alloys Fabricated by Spark Plasma Sintering

被引：0

作者：

Li, Xiaoqiang ^{[1
]}

Hu, Ke ^{[1
]}

Chen, Zhicheng ^{[1
]}

Xin, Hongwei ^{[1
]}

机构：

[1] S China Univ Technol, Natl Metall Mat Net Shape Forming Engn Res Ctr, Guangzhou 510640, Guangdong, Peoples R China

来源：

EMERGING FOCUS ON ADVANCED MATERIALS, PTS 1 AND 2 | 2011年 / 306-307卷

关键词：

Spark Plasma Sintering; W-9.8Ni-4.2Fe; mechanical property; TUNGSTEN HEAVY ALLOY; MECHANICAL-PROPERTIES; MICROSTRUCTURE;

D O I：

10.4028/www.scientific.net/AMR.306-307.509

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of sintering temperature on the properties of W-9.8Ni-4.2Fe alloys fabricated by spark plasma sintering were studied. The peak, base, repetition frequency of pulse electric current and the initial average no-load current were chosen as 3000A, 360A, 50Hz and 1200A during the sintering process, respectively. Research results show that W-9.8Ni-4.2Fe alloy, consolidated by SPSing for 6min at 1250 degrees C under a pressure of 30MPa, has a relative density of 97.72%, hardness of 41.8HRC, transverse rupture strength of 1443MPa, and compression strength of 2640MPa. Its combination properties are topmost among all specimens sintered at various temperatures, which is attributable to the microstructural characteristics of dense microstructure, uniform distribution of binder, low connectivity of W-W and good metallurgic bonding. The optimal fracture surface in relation to the microstructure is dominating tungsten intergranular fracture, accompanied by local transgranular fracture in tungsten phase and ductile avulsion of the binder phase.

引用

页码：509 / 513

页数：5

共 11 条

[1] An investigation on the solid state sintering of mechanically alloyed nano-structured 90W-Ni-Fe tungsten heavy alloy [J].

Akhtar, Farid .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2008, 26 (03) :145-151

[2]

[Anonymous], TUNGSTEN TUNGSTEN AL

[3]

Chen Y, 2000, ENVIRONMENT CONSCIOUS MATERIALS - ECOMATERIALS, P699

[4] FRACTURE-BEHAVIOR OF W-NI-FE HEAVY ALLOYS [J].

CHURN, KS ;

GERMAN, RM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (02) :331-338

[5] Sintering activation by external electrical field [J].

Groza, JR ;

Zavaliangos, A .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 287 (02) :171-177

[6] Microstructure and Mechanical Properties of SPSed (Spark Plasma Sintered) Ti66Nb13Cu8Ni6.8Al6.2 Bulk Alloys with and without WC Addition [J].

Li, Xiaoqiang ;

Yang, Chao ;

Chen, Weiping ;

Qu, Shengguan ;

Li, Yuanyuan .

MATERIALS TRANSACTIONS, 2009, 50 (07) :1720-1724

[7] Microstructure and mechanical properties of mechanically alloyed and solid-state sintered tungsten heavy alloys [J].

Ryu, HJ ;

Hong, SH ;

Baek, WH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 291 (1-2) :91-96

[8]

Schubert W. D., 1992, International Journal of Refractory & Hard Metals, V11, P151, DOI 10.1016/0263-4368(92)90057-9

[9]

Upadhyaya A, 2007, SCRIPTA MATER, V56, P5, DOI 10.1016/j.scriptmat.2006.09.010

[10]

Wang CB, 2002, J MATER SCI TECHNOL, V18, P234

← 1 2 →