Influence of Nano-scaled Zirconia Particles on the Electrical Properties of Polymer Insulating Materials

被引：12

作者：

Albayrak, S. ^{[1
]}

Becker-Willinger, C. ^{[1
]}

Aslan, M. ^{[1
]}

Veith, M. ^{[1
]}

机构：

[1] INM Leibniz Inst New Mat, D-66123 Saarbrucken, Germany

来源：

IEEE TRANSACTIONS ON DIELECTRICS AND ELECTRICAL INSULATION | 2012年 / 19卷 / 01期

关键词：

Polymer nanocomposites; polyurethane; nanoparticles; defect structure; insulation; partial discharge stability; dielectric breakdown; mechanical properties; colloidal processing;

D O I：

10.1109/TDEI.2012.6148504

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

In the present work the influence of nano-scaled zirconia particles with different structures on the structural and electrical properties of polyurethane (PU) insulating coatings was investigated. PU matrix insulating coatings containing non-doped and 4 mole % yttrium doped nano-scaled zirconia with average particle size between 12 and 13 nm were prepared by wet chemical methods. High resolution transmission electron microscopy analysis of thermally cured composites showed that the nano dispersed zirconia particles were uniformly distributed within matrix. Incorporation of 5 vol. % nanoparticles into the PU matrix resulted in a slight increase of the micro hardness and elastic modulus. The effect of zirconia filling (non-doped and doped) on the electrical breakdown strength was not observed. But, a strong influence of the nanoparticle addition on the partial discharge stability was detected. Partial discharge breakdown time for non-filled PU matrix was 2.5 h, for PU filled with non-doped zirconia 65 h and for PU filled with yttrium doped zirconia > 100 h, respectively. The additional benefit of doped zirconia may be explained by its different electronic structure and polarisation behaviour.

引用

页码：76 / 82

页数：7

共 23 条

[1]

Albayrak S., 2006, German patent, Patent No. [DE 10 2006 041 738 A1, 102006041738]

[2]

Bergman W., 1989, WERKSTOFFTECHNIK GRU

[3]

Bohm F.R., 2005, US Patent, Patent No. [US6908692 B1, 6908692]

[4]

Kindersberger J., 2005, ETG FACHBERICHT, P7

[5]

Kinloch A.J., 1983, DURABILITY STRUCTURA

[6]

Kinloch A.J., 1987, Adhesion and Adhesives: Science and Technology

[7]

Lewis TJ, 2004, PROCEEDINGS OF THE 2004 IEEE INTERNATIONAL CONFERENCE ON SOLID DIELECTRICS, VOLS 1 AND 2, P792

[8] Dielectric properties of polylmide/Al2O3 hybrids synthesized by in-situ polymerization [J].

Li, Hongyan ;

Liu, Gang ;

Liu, Bin ;

Chen, Wei ;

Chen, Shoutian .

MATERIALS LETTERS, 2007, 61 (07) :1507-1511

[9]

Mondal P., 1998, THESIS DARMSTADT TEC

[10] Nanocomposite dielectrics - properties and implications [J].

Nelson, JK ;

Hu, Y .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2005, 38 (02) :213-222

← 1 2 3 →