An investigation on hot corrosion behavior of YSZ-Ta2O5 in Na2SO4+V2O5 salt at 1100 °C

被引：93
作者：
Habibi, M. H. [1 ]
Wang, Li [1 ]
Liang, Jiandong [1 ]
Guo, S. M. [1 ]
机构：
[1] Louisiana State Univ, Baton Rouge, LA 70803 USA
来源：
CORROSION SCIENCE | 2013年 / 75卷
关键词：
Thermal barrier coating (TBC); YSZ; Tantalum oxide; Hot corrosion; THERMAL BARRIER COATINGS; YTTRIA; YSZ; DEGRADATION; RESISTANCE; STABILITY; CERIA; EVOLUTION; LAYER;
D O I：
10.1016/j.corsci.2013.06.025
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study compares the hot corrosion performance of yttria stabilized zirconia (YSZ), and YSZ-Ta2O5 (TaYSZ) composite samples in the presence of molten mixture of Na2SO4 + V2O5 at 1100 degrees C. For YSZ, the reaction between NaVO3 and Y2O3 produces YVO4 and leads to the transformation of tetragonal ZrO2 to monoclinic ZrO2. For TaYSZ, minor amounts of NaTaO3, TaVO5 and Ta9VO25 are formed as the hot corrosion products with only traceable amounts of YVO4. Due to the synergic effect of doping of zirconia with both Y2O3 and Ta2O5, the TaYSZ sample has a much better hot corrosion resistance than YSZ. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：409 / 414
页数：6
相关论文
共 40 条
[21]   Some aspects of the hot corrosion of thermal barrier coatings [J].
Jones, RL .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1997, 6 (01) :77-84
[22]   Emerging materials and processes for thermal barrier systems [J].
Levi, CG .
CURRENT OPINION IN SOLID STATE & MATERIALS SCIENCE, 2004, 8 (01) :77-91
[23]   Hot corrosion behaviour of Yb2Zr2O7 ceramic coated with V2O5 at temperatures of 600-800 °C in air [J].
Li, Sa ;
Liu, Zhan-Guo ;
Ouyang, Jia-Hu .
CORROSION SCIENCE, 2010, 52 (10) :3568-3572
[24]   Degradation of yttria-stabilized zirconia thermal barrier coatings by vanadium pentoxide, phosphorous pentoxide, and sodium sulfate [J].
Mohan, Prabhakar ;
Yuan, Biao ;
Patterson, Travis ;
Desai, Vimal H. ;
Sohn, Yongho H. .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (11) :3601-3607
[25]   Microscopic observation of degradation behavior in yttria and ceria stabilized zirconia thermal barrier coatings under hot corrosion [J].
Park, SY ;
Kim, JH ;
Kim, MC ;
Song, HS ;
Park, CG .
SURFACE & COATINGS TECHNOLOGY, 2005, 190 (2-3) :357-365
[26]   Opportunities for TBCs in the ZrO2-YO1.5-TaO2.5 system [J].
Pitek, Felicia M. ;
Levi, Carlos G. .
SURFACE & COATINGS TECHNOLOGY, 2007, 201 (12) :6044-6050
[27]   Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings [J].
Rabiei, A ;
Evans, AG .
ACTA MATERIALIA, 2000, 48 (15) :3963-3976
[28]   Ta2O5/Nb2O5 and Y2O3 co-doped zirconias for thermal barrier coatings [J].
Raghavan, S ;
Wang, H ;
Dinwiddie, RB ;
Porter, WD ;
Vassen, R ;
Stöver, D ;
Mayo, MJ .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2004, 87 (03) :431-437
[29]   The hot corrosion resistance of 20 mol% YTaO4 stabilized tetragonal zirconia and 14 mol% Ta2O5 stabilized orthorhombic zirconia for thermal barrier coating applications [J].
Raghavan, S ;
Mayo, MJ .
SURFACE & COATINGS TECHNOLOGY, 2002, 160 (2-3) :187-196
[30]   Thermal properties of zirconia co-doped with trivalent and pentavalent oxides [J].
Raghavan, S ;
Wang, H ;
Porter, WD ;
Dinwiddie, RB ;
Mayo, MJ .
ACTA MATERIALIA, 2001, 49 (01) :169-179
1234