An investigation on hot corrosion behavior of YSZ-Ta2O5 in Na2SO4+V2O5 salt at 1100 °C

被引：89
作者：
Habibi, M. H. [1 ]
Wang, Li [1 ]
Liang, Jiandong [1 ]
Guo, S. M. [1 ]
机构：
[1] Louisiana State Univ, Baton Rouge, LA 70803 USA
来源：
CORROSION SCIENCE | 2013年 / 75卷
关键词：
Thermal barrier coating (TBC); YSZ; Tantalum oxide; Hot corrosion; THERMAL BARRIER COATINGS; YTTRIA; YSZ; DEGRADATION; RESISTANCE; STABILITY; CERIA; EVOLUTION; LAYER;
D O I：
10.1016/j.corsci.2013.06.025
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study compares the hot corrosion performance of yttria stabilized zirconia (YSZ), and YSZ-Ta2O5 (TaYSZ) composite samples in the presence of molten mixture of Na2SO4 + V2O5 at 1100 degrees C. For YSZ, the reaction between NaVO3 and Y2O3 produces YVO4 and leads to the transformation of tetragonal ZrO2 to monoclinic ZrO2. For TaYSZ, minor amounts of NaTaO3, TaVO5 and Ta9VO25 are formed as the hot corrosion products with only traceable amounts of YVO4. Due to the synergic effect of doping of zirconia with both Y2O3 and Ta2O5, the TaYSZ sample has a much better hot corrosion resistance than YSZ. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：409 / 414
页数：6
相关论文
共 40 条
  • [1] A comparative study on hot corrosion resistance of three types of thermal barrier coatings:: YSZ, YSZ + Al2O3 and YSZ/Al2O3
    Afrasiabi, Abbas
    Saremi, Mohsen
    Kobayashi, Akira
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2): : 264 - 269
  • [2] Hot corrosion control in plasma sprayed YSZ coating by alumina layer with evaluation of microstrcuture and nanoindentation data (H, E)
    Afrasiabi, Abbas
    Kobayashi, Akira
    [J]. VACUUM, 2013, 88 : 103 - 107
  • [3] Evaluation of hot corrosion behavior of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coatings in the presence of Na2SO4+V2O5 molten salt
    Ahmadi-Pidani, Raheleh
    Shoja-Razavi, Reza
    Mozafarinia, Reza
    Jamali, Hossein
    [J]. CERAMICS INTERNATIONAL, 2012, 38 (08) : 6613 - 6620
  • [4] Thermal cycling resistance of modified thick thermal barrier coatings
    Ahmaniemi, S
    Vuoristo, P
    Mäntylä, T
    Gualco, C
    Bonadei, A
    Di Maggio, R
    [J]. SURFACE & COATINGS TECHNOLOGY, 2005, 190 (2-3) : 378 - 387
  • [5] Modified thick thermal barrier coatings:: Microstructural characterization
    Ahmaniemi, S
    Vippola, M
    Vuoristo, P
    Mäntylä, T
    Cernuschi, F
    Lutterotti, L
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (08) : 2247 - 2258
  • [6] Ta2O5-Y2O3-ZrO2 system: Experimental study and preliminary thermodynamic description
    Bhattacharya, Anup K.
    Shklover, Valery
    Steurer, Walter
    Witz, Gregoire
    Bossmann, Hans-peter
    Fabrichnaya, Olga
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2011, 31 (03) : 249 - 257
  • [7] Effect of 7YSZ on the long-term stability of YTaO4 doped ZrO2 system
    Bhattachaya, Anup
    Shklover, Valery
    Kunze, Karsten
    Steurer, Walter
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2011, 31 (15) : 2897 - 2901
  • [8] THERMAL-PROPERTIES OF CERIA AND YTTRIA PARTIALLY STABILIZED ZIRCONIA THERMAL BARRIER COATINGS
    BRANDON, JR
    TAYLOR, R
    [J]. SURFACE & COATINGS TECHNOLOGY, 1989, 39 (1-3) : 143 - 151
  • [9] PHASE-STABILITY OF ZIRCONIA-BASED THERMAL BARRIER COATINGS .2. ZIRCONIA CERIA ALLOYS
    BRANDON, JR
    TAYLOR, R
    [J]. SURFACE & COATINGS TECHNOLOGY, 1991, 46 (01) : 91 - 101
  • [10] Environmental stability of the YSZ layer and the YSZ/TGO interface of an in-service EB-PVD coated high-pressure turbine blade
    Braue, Wolfgang
    [J]. JOURNAL OF MATERIALS SCIENCE, 2009, 44 (07) : 1664 - 1675
1234