Influence of initial surface condition of lithium metal anodes on surface modification with HF

被引:0
|
作者
Shiraishi, S [1 ]
Kanamura, K [1 ]
Takehara, ZI [1 ]
机构
[1] Kyoto Univ, Grad Sch Engn, Dept Energy & Hydrocarbon Chem, Sakyo Ku, Kyoto 60601, Japan
关键词
HF; lithium electrodes; surface modification; XPS measurements;
D O I
暂无
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Surface modification of as-received lithium foils was carried out using acid-base reactions of the native surface films on lithium metal with HF. Two types of as-received lithium foils covered with different native films were used as samples for this surface modification. One was a lithium foil having a very thin native surface film and the other one had a thicker native surface film. The surface condition of the lithium metal was analysed by X-ray photoelectron spectroscopy before and after the surface modification using HF, and the coulombic efficiency was measured electrochemically. The thickness of the surface film on the modified lithium foils was related to the Li2O layer thickness in the native film on the as-received lithium foils. The modified lithium foil which had the thinner native surface film provided more uniform deposition of lithium and a higher coulombic efficiency during charge and discharge cycles when propylene carbonate electrolyte with 1.0 M LiPF6 was used as the electrolyte. These results show that the initial condition of the native surface film plays an important role in surface modification with HF.
引用
收藏
页码:869 / 881
页数:13
相关论文
共 50 条
  • [1] Influence of initial surface condition of lithium metal anodes on surface modification with HF
    S. Shiraishi
    K. Kanamura
    Z-I. Takehara
    Journal of Applied Electrochemistry, 1999, 29 (7) : 867 - 879
  • [2] Functionalizing the Surface of Lithium-Metal Anodes
    Buonaiuto, Megan
    Neuhold, Susanna
    Schroeder, David J.
    Lopez, Carmen M.
    Vaughey, John T.
    CHEMPLUSCHEM, 2015, 80 (02): : 363 - 367
  • [3] Surface engineering toward stable lithium metal anodes
    Lu, Gongxun
    Nai, Jianwei
    Luan, Deyan
    Tao, Xinyong
    Lou, Xiong Wen
    SCIENCE ADVANCES, 2023, 9 (14)
  • [4] Nanoscale surface modification of polymer nanofibers enables uniform lithium nucleation and deposition for stable lithium metal anodes
    Su, Zhengkang
    Zhang, Jingjing
    Jin, Junhong
    Yang, Shenglin
    Li, Guang
    Chemical Engineering Journal, 2022, 430
  • [5] Nanoscale surface modification of polymer nanofibers enables uniform lithium nucleation and deposition for stable lithium metal anodes
    Su, Zhengkang
    Zhang, Jingjing
    Jin, Junhong
    Yang, Shenglin
    Li, Guang
    CHEMICAL ENGINEERING JOURNAL, 2022, 430
  • [6] Surface modification of carbon anodes for secondary lithium battery by fluorination
    Nakajima, Tsuyoshi
    JOURNAL OF FLUORINE CHEMISTRY, 2007, 128 (04) : 277 - 284
  • [7] Surface modification of carbon anodes for lithium ion batteries by fluorine
    Nakajima, Tsuyoshi
    Naga, Kazuhisa
    Achiha, Takashi
    Ohzawa, Yoshimi
    Tressaud, Alain
    Mazej, Zoran
    Zemva, Boris
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2014, 248
  • [8] Surface modification of rice husk ash as anodes for lithium ion batteries
    Chaikawang, Chirapan
    Hongthong, Rattiya
    Kaewmala, Songyoot
    Pongha, Sarawut
    Kanapan, Yutthanakorn
    Meethong, Nonglak
    MATERIALS TODAY-PROCEEDINGS, 2018, 5 (06) : 13989 - 13994
  • [9] 3D composite lithium metal with multilevel micro-nano structure combined with surface modification for stable lithium metal anodes
    Jia, Weishang
    Li, Hudong
    Wang, Zihao
    Liu, Yuchi
    Yang, Yao-Yue
    Li, Jingze
    APPLIED SURFACE SCIENCE, 2021, 570
  • [10] Fingermark visualisation on metal surfaces: An initial investigation of the influence of surface condition on process effectiveness
    Pitera, M.
    Sears, V. G.
    Bleay, S. M.
    Park, S.
    SCIENCE & JUSTICE, 2018, 58 (05) : 372 - 383