The effect of heat treatment on recrystallized microstructure, precipitation and ductility of hot-rolled Fe-Cr-Al-REM ferritic stainless steel sheets

被引:32
作者
Qu, H. P. [1 ]
Lang, Y. P. [1 ]
Yao, C. F. [1 ,2 ]
Chen, H. T. [1 ]
Yang, C. Q. [1 ]
机构
[1] Cent Iron & Steel Res Inst, Inst Special Steets Formerly Inst Struct Mat, Beijing 100081, Peoples R China
[2] Cent Iron & Steel Res Inst, Zhuozhou 072750, Hebei, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 562卷
关键词
Electron microscopy; Ferrous alloy; Sheet forming; Precipitation; HIGH-TEMPERATURE OXIDATION; ALLOY THIN STRIP; CORROSION BEHAVIOR; AL2O3; SCALES; FE-20CR-5AL; DIFFUSION; GROWTH; FABRICATION; RESISTANCE; YTTRIUM;
D O I
10.1016/j.msea.2012.11.008
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
This study presents research works about the effects of heat treatment on recrystallized equiaxed grain size, precipitation, room temperature (RT) toughness and ductile to brittle transition temperature (DBTT) of Fe-Cr-Al-REM ferritic stainless steel (FSS) hot-rolled sheet Results showed that the recrystallization of hot-rolled Fe-Cr-Al-REM FSS sheet could be completed after annealing treatment at 750 degrees C for 15 min with the equiaxed grain diameter of approximately 50 mu m. Inappropriate annealing treatment would inevitably leads to the unexpected grain coarsening. On the other hand, a great deal of needle-like or spot-like fine aluminum-lanthanum compound Al11La3 precipitates were observed in the ferrite matrix after 1 h aging treatment at 750 C. The microstructure observation results associated with the impact test definitely illustrated that the Al11La3 precipitates was the reason for the brittle crack in the as-casted ingot and as-forged slab. The real DBTT of the annealed Fe-Cr-AI-REM FSS sheet with average grain size of about 50 mu m was -4 degrees C. Meanwhile, the DBTT of the hot-rolled Fe-Cr-Al-REM stainless steel sheet was evidently increased as the recrystallized grain size increased. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:9 / 16
页数:8
相关论文
共 27 条
[1]   High temperature oxidation of Fe-Al and Fe-Cr-Al alloys: The role of Cr as a chemically active element [J].
Airiskallio, E. ;
Nurmi, E. ;
Heinonen, M. H. ;
Vayrynen, I. J. ;
Kokko, K. ;
Ropo, M. ;
Punkkinen, M. P. J. ;
Pitkanen, H. ;
Alatalo, M. ;
Kollar, J. ;
Johansson, B. ;
Vitos, L. .
CORROSION SCIENCE, 2010, 52 (10) :3394-3404
[2]   INFLUENCE OF YTTRIUM AND METHOD OF FABRICATION ON THE OXIDATION BEHAVIOR OF FE-CR-AL ALLOYS AT HIGH-TEMPERATURE IN AIR [J].
CLEMENDOT, F ;
GRAS, JM ;
VANDUYSEN, JC ;
ZACHARIE, G .
CORROSION SCIENCE, 1993, 35 (5-8) :901-908
[3]   New approximant phases in Al-Cr-Fe [J].
Demange, V ;
Wu, JS ;
Brien, V ;
Machizaud, F ;
Dubois, JM .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 294 :79-81
[4]   Creep and tensile behaviors of Fe-Cr-Al foils and laser microwelds at high temperature [J].
El Kadiri, H ;
Bienvenu, Y ;
Solanki, K ;
Horstemeyer, MF ;
Wang, PT .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 421 (1-2) :168-181
[5]   Effect of rare-earth elements on high-temperature oxidation resistance of Fe-20Cr-5Al alloy foils [J].
Ishii, K ;
Kohno, M ;
Ishikawa, S ;
Satoh, S .
MATERIALS TRANSACTIONS JIM, 1997, 38 (09) :787-792
[6]  
Ishii K., 1999, KAWASAKI STEEL TECHN, V40, P30
[7]  
Itoh I.
[8]  
., 1995, NIPPON STEEL TECH RE, V64, P69
[9]   Thermodynamics and diffusion in ternary Fe-Al-Cr alloys, Part I: Thermodynamic modeling [J].
Jacobs, M. H. G. ;
Schmid-Fetzer, R. ;
Markus, T. ;
Motalov, V. ;
Borchardt, G. ;
Spitzer, K. -H. .
INTERMETALLICS, 2008, 16 (08) :995-1005
[10]   Growth of α-alumina oxide film in high temperature oxidation of Fe-20Cr-5Al alloy thin strip [J].
Lee, KS ;
Oh, KH ;
Park, WW ;
Ra, HY .
SCRIPTA MATERIALIA, 1998, 39 (08) :1151-1155