Evolution of discontinuous/continuous Al3(Sc,Zr) precipitation in Al-Mg-Mn 5083 alloy during thermomechanical process and its impact on tensile properties

被引:26
作者
Algendy, Ahmed Y. [1 ]
Liu, Kun [1 ]
Rometsch, Paul [2 ]
Parson, Nick [2 ]
Chen, Grant [1 ]
机构
[1] Univ Quebec Chicoutimi, Dept Appl Sci, Saguenay, PQ G7H 2B1, Canada
[2] Arvida Res & Dev Ctr, Rio Tinto Aluminum, Saguenay, PQ G7S 4K8, Canada
基金
加拿大自然科学与工程研究理事会;
关键词
Al-Mg-Mn; 5083; alloy; Discontinuous Al 3 (Sc; Zr) precipitation; Sc and Zr addition; Microstructure; Mechanical properties; MECHANICAL-PROPERTIES; PHASE PRECIPITATION; ZR; SC; MICROSTRUCTURE; BEHAVIOR; SCANDIUM; KINETICS; AMBIENT;
D O I
10.1016/j.matchar.2022.112241
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The evolution of discontinuous and continuous Al3(Sc,Zr) precipitation in an Al-Mg-Mn AA5083 alloy during heat treatment and hot rolling was investigated. The results showed that, at a high Sc content (0.43 wt%), a large number of line/fan-shaped structures were formed as discontinuous Al3(Sc,Zr) precipitation during solidification, while no such discontinuous precipitation was observed when the amount of Sc added was low (0.15 wt%). During the three-step heat treatment (275 C /12 h + 375 C/48 h + 425 C/12 h), two types of precipitates - Mn-bearing dispersoids and spherical Al3(Sc,Zr) precipitates - were formed as the main strengthening phases. In the high-Sc alloy, the discontinuous Al3(Sc,Zr) precipitates dissolved partially. However, the quantity of the spherical Al3(Sc,Zr) precipitates in the high-Sc alloy was much lower than that in the low-Sc alloy, which degraded its aging hardening response. During hot rolling, although the discontinuous precipitates were completely dissolved, the number density of the spherical Al3(Sc,Zr) precipitates in the high-Sc alloy was still lower than that in the low-Sc alloy. The tensile properties of the Sc-containing alloys improved significantly compared with those of the base alloy. However, the yield and ultimate tensile strengths of the high-Sc alloy were lower than those of the low-Sc alloy. This indicates that the discontinuous precipitation had a deleterious effect on the mechanical properties of the alloy.
引用
收藏
页数:10
相关论文
共 39 条
[1]   Evolution of dispersoids during multistep heat treatments and their effect on rolling performance in an Al-5% Mg-0.8% Mn alloy [J].
Algendy, Ahmed Y. ;
Liu, Kun ;
Chen, X. Grant .
MATERIALS CHARACTERIZATION, 2021, 181
[2]   FOIL THICKNESS MEASUREMENTS FROM CONVERGENT-BEAM DIFFRACTION PATTERNS [J].
ALLEN, SM .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1981, 43 (02) :325-335
[3]   Precipitation behavior of strip cast Al-Mg-0.4Sc-0.15Zr alloy under single and multiple-stage aging processes [J].
Anijdan, S. H. Mousavi ;
Kang, D. ;
Singh, N. ;
Gallerneault, M. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 640 :275-279
[4]   CONSTITUTION AND AGE HARDENING OF AL-SC ALLOYS [J].
BLAKE, N ;
HOPKINS, MA .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (08) :2861-2867
[5]   Influence of severe plastic deformations on secondary phase precipitation in a 6082 Al-Mg-Si alloy [J].
Cabibbo, M ;
Evangelista, E ;
Vedani, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (05) :1353-1364
[6]   Effect of solidification cooling rate on kinetics of continuous/discontinuous Al3(Sc,Zr) precipitation and the subsequent age-hardening response in cold-rolled AlMgSc(Zr) sheets [J].
Dong, Qingshan ;
Howells, Andrew ;
Lloyd, David J. ;
Gallerneault, Mark ;
Fallah, Vahid .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 772
[7]   Diffusion coefficients of some solutes in fcc and liquid Al: critical evaluation and correlation [J].
Du, Y ;
Chang, YA ;
Huang, BY ;
Gong, WP ;
Jin, ZP ;
Xu, HH ;
Yuan, ZH ;
Liu, Y ;
He, YH ;
Xie, FY .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 363 (1-2) :140-151
[8]   Mechanical properties of Al(Sc,Zr) alloys at ambient and elevated temperatures [J].
Fuller, CB ;
Seidman, DN ;
Dunand, DC .
ACTA MATERIALIA, 2003, 51 (16) :4803-4814
[9]   Temporal evolution of the nanostructure of AI(Sc,Zr) alloys:: Part I -: Chemical compositions of Al3(Sc1-xZrx) precipitatesy [J].
Fuller, CB ;
Murray, JL ;
Seidman, DN .
ACTA MATERIALIA, 2005, 53 (20) :5401-5413
[10]   SYSTEMATICS OF CELLULAR PRECIPITATION REACTIONS [J].
HORNBOGEN, E .
METALLURGICAL TRANSACTIONS, 1972, 3 (11) :2717-+