Resistance to slurry erosion by WC-10Co-4Cr and Cr3C2-25(Ni20Cr) coatings deposited by HVOF stainless steel F6NM

被引：19

作者：

Maekai, Ishfaq Amin ^{[1
]}

Harmain, G. A. ^{[1
]}

Zehab-ud-Din ^{[1
]}

Masoodi, J. H. ^{[2
]}

机构：

[1] Natl Inst Technol, Dept Mech Engn, Turbine Eros Testing Lab, Srinagar 190006, Kashmir, India

[2] Univ Kashmir, Inst Technol, Dept Mech Engn, Srinagar 190006, Kashmir, India

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2022年 / 105卷

关键词：

HVOF; Slurry erosion; Dul-Hasti; Tungsten; Sand; WC-CO COATINGS; PARTICLE-SIZE; CAVITATION EROSION; ABRASION WEAR; SAND EROSION; SLIDING WEAR; BEHAVIOR; VELOCITY; FLOW; PERFORMANCE;

D O I：

10.1016/j.ijrmhm.2022.105830

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Hydroelectric turbine machinery experience extreme wear and tear due to slurry erosion and is one of the leading causes for the unplanned shutdown of hydro power plants. The coatings produced by High-velocity oxy-fuel (HVOF) thermal spray process on different hydro-turbine parts is known for improving wear resistance. In the present study, WC-10Co-4Cr and Cr3C2 - 25(Ni20Cr) coatings were sprayed by HVOF process on F6NM stainless steel of Dul-Hasti hydro-power plant turbine material. The slurry erosive wear studies of developed coatings was performed using high speed slurry erosive wear tester. Sediments collected from Dul-Hasti power plant dam site was taken as erodent material. The effect of four parameters specifically rotational speed (500-1250 rpm), slurry concentration (25-40 wt%), sand particle size (125-425 mu m), and test duration (450-900 min) on slurry erosion of coated materials was studied. It was observed that among all the developed three coatings, the WC-10Co-4Cr coated samples has shown superior erosion resistance compared to Cr3C2 - 25(Ni20Cr) coated samples due to its improved micro-hardness. Both the developed coatings were observed to be useful in enhancing the erosion resistance of F6NM steel significantly. Erosion mechanism were studied in detail using SEM. The properties such as hardness and porosity were also examined.

引用

页数：9

共 62 条

[1] Some studies on slurry erosion of flame sprayed Ni-Cr-Si-B coating
Arji, Rambabu
Dwivedi, D. K.
Gupta, S. R.
[J]. INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2009, 61 (01) : 4 - 10
[2] Arsenault B, 2001, THERMAL SPRAY 2001: NEW SURFACES FOR A NEW MILLENNIUM, P1051
[3] Sand erosion of Pelton turbine nozzles and buckets: A case study of Chilime Hydropower Plant
Bajracharya, T. R.
Acharya, B.
Joshi, C. B.
Saini, R. R.
Dahhaug, O. G.
[J]. WEAR, 2008, 264 (3-4) : 177 - 184
[4] Toughness and microstructure of 13Cr4NiMo high-strength steel welds
Bilmes, P
Llorente, C
Ipina, JP
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2000, 9 (06) : 609 - 615
[5] Experimental Study of Erosion Wear in a Centrifugal Slurry Pump Using Coriolis Wear Test Rig
Chandel, Sunil
Singh, S. N.
Seshadri, V.
[J]. PARTICULATE SCIENCE AND TECHNOLOGY, 2012, 30 (02) : 179 - 195
[6] Erosion behaviour of hydro turbine steels
Chauhan, Akhilesh K.
Goel, D. B.
Prakash, Satya
[J]. BULLETIN OF MATERIALS SCIENCE, 2008, 31 (02) : 115 - 120
[7] Study of the simultaneous effects of secondary flow and sediment erosion in Francis turbines
Chitrakar, Sailesh
Neopane, Hari Prasad
Dahlhaug, Ole Gunnar
[J]. RENEWABLE ENERGY, 2016, 97 : 881 - 891
[8] SPECIMEN DIAMETER, IMPACT VELOCITY, EROSION RATE AND PARTICLE DENSITY IN A SLURRY POT EROSION TESTER
CLARK, HM
[J]. WEAR, 1993, 162 : 669 - 678
[9] The microstructure of WC-Co coatings produced by HVOF spraying with liquid fuel
Coulson, W
Harris, SJ
[J]. TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1997, 75 : 108 - 112
[10] Slurry Erosion Behavior of F6NM Stainless Steel and High-Velocity Oxygen Fuel-Sprayed WC-10Co-4Cr Coating
Cui, S. Y.
Miao, Q.
Liang, W. P.
Huang, B. Z.
Ding, Z.
Chen, B. W.
[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2017, 26 (03) : 473 - 482

← 1 2 3 4 5 6 7 →