Selective Catalytic Reduction of NOx on Cr-Mn Mixed Oxide at Low Temperature

被引：0
|
作者：
Chen Zhihang [1 ,2 ]
Li Xuehui [2 ]
Cen Chaoping [1 ]
Gao Xiang [2 ]
Wang Lefu [2 ]
机构：
[1] Minist Environm Protect, South China Inst Environm Sci, Guangzhou 510655, Guangdong, Peoples R China
[2] South China Univ & Technol, Green Chem Prod Technol, Sch Chem & Chem Engn, Guangdong Provincial Key Lab Green, Guangzhou 510640, Guangdong, Peoples R China
来源：
FUNDAMENTAL OF CHEMICAL ENGINEERING, PTS 1-3 | 2011年 / 233-235卷
关键词：
Cr-Mn mixed oxides; CrMn1.5O4; low-temperature; selective catalytic reduction; NOx; NH3; NH3; H-2;
D O I：
10.4028/www.scientific.net/AMR.233-235.1564
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The solid state reaction method, coprecipitation method and citric acid method were employed for the preparation of Cr-Mn mixed-oxide catalysts. Experimental results showed that this catalytic system has good selective catalytic reduction (SCR) properties of NOx by ammonia in the presence of excess oxygen at low temperature (80-220 degrees C). 97.8% conversion of NOx with 100% selectivity of N-2 had been achieved on Cr-MnOx mixed oxide prepared by the citric acid method at 120 degrees C with the space velocity of 30,000 h(-1). X-ray diffraction, BET were adopted for the characterization of the active phase. The characterization results showed that a new crystal phase CrMn1.5O4 generated in mixed oxides which was the active center of the Cr-Mn catalysts.
引用
收藏
页码：1564 / +
页数：2
相关论文
共 50 条
  • [11] Research progress on Mn-based catalysts for low-temperature selective catalytic reduction of NOx
    Zheng, Yu-Ying
    Wang, Xie
    Gongneng Cailiao/Journal of Functional Materials, 2014, 45 (11): : 11008 - 11012
  • [12] Study on carbon catalyst for selective catalytic reduction of NOx at low temperature
    Gou, Xiang
    Zhang, Kai
    Liu, Liansheng
    Liu, Wenyong
    Wang, Zifang
    Yang, Guang
    Wu, Jinxiang
    Wang, Enyu
    RENEWABLE ENERGY AND ENVIRONMENTAL TECHNOLOGY, PTS 1-6, 2014, 448-453 : 868 - 873
  • [13] Selective catalytic reduction of NOx with NH3 over Mn-Zr-Ti mixed oxide catalysts
    Zhang, Bolin
    Liebau, Michael
    Liu, Bo
    Li, Lin
    Zhang, Shengen
    Glaeser, Roger
    JOURNAL OF MATERIALS SCIENCE, 2019, 54 (09) : 6943 - 6960
  • [14] New Mn-TiO2 aerogel catalysts for the low-temperature selective catalytic reduction of NOx
    Jihene Arfaoui
    Abdelhamid Ghorbel
    Carolina Petitto
    Gerard Delahay
    Journal of Sol-Gel Science and Technology, 2021, 97 : 302 - 310
  • [15] New Mn-TiO2 aerogel catalysts for the low-temperature selective catalytic reduction of NOx
    Arfaoui, Jihene
    Ghorbel, Abdelhamid
    Petitto, Carolina
    Delahay, Gerard
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2021, 97 (02) : 302 - 310
  • [16] Redox on Mn-Ce interface and its effects on low temperature selective catalytic reduction for NOx removal
    Liu, Fengyuan
    Li, Junqi
    Sohn, Hong Yong
    Chen, Chaoyi
    Yang, Jian
    Liu, Xudong
    Lan, Yuanpei
    Zhang, Wei
    Wang, Qin
    Liu, Li
    FUEL, 2023, 350
  • [17] Selective catalytic reduction of NOx by low-temperature NH3 over MnxZr1 mixed-oxide catalysts
    Zhang, Shuaibo
    Li, Haixia
    Zhang, Anchao
    Sun, Zhijun
    Zhang, Xinmin
    Yang, Changze
    Jin, Leying
    Song, Zhiheng
    RSC ADVANCES, 2022, 12 (03) : 1341 - 1351
  • [18] Novel Mn-Ce-Ti Mixed-Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3
    Liu, Zhiming
    Zhu, Junzhi
    Li, Junhua
    Ma, Lingling
    Woo, Seong Ihl
    ACS APPLIED MATERIALS & INTERFACES, 2014, 6 (16) : 14500 - 14508
  • [19] Experimental Study on Selective Catalytic Reduction of NOx With CO at Low-Temperature
    Liu K.-J.
    Yu Q.-B.
    Wang K.-M.
    Wang C.-P.
    Dongbei Daxue Xuebao/Journal of Northeastern University, 2017, 38 (07): : 972 - 977
  • [20] Recent Progress on Low-Temperature Selective Catalytic Reduction of NOx with Ammonia
    Park, Eun Duck
    MOLECULES, 2024, 29 (18):
12345