Sintering and properties of magnesium orthosilicate ceramic

被引：5

作者：

Chin, K. L. Jeffrey ^{[1
]}

Ramesh, S. ^{[1
]}

Chew, W. J. Kelvin ^{[2
]}

Ganesan, P. ^{[1
]}

Bang, L. T. ^{[1
]}

Ching, Y. C. ^{[1
]}

Niakan, A. ^{[1
]}

Tan, C. Y. ^{[1
]}

Purbolaksono, J. ^{[1
]}

Teng, W. D. ^{[3
]}

机构：

[1] Univ Malaya, Dept Mech Engn, Ctr Adv Mfg & Mat Proc, Kuala Lumpur 50603, Malaysia

[2] Taylors Univ, Sch Engn, Subang Jaya 47500, Malaysia

[3] SIRIM Berhad, Ceram Technol Grp, Shah Alam 40911, Malaysia

来源：

CERAMICS INTERNATIONAL | 2015年 / 41卷 / 10期

关键词：

Sintering; Mechanical properties; Magnesium orthosilicate; FORSTERITE CERAMICS; NANOSTRUCTURE FORSTERITE; MECHANICAL ACTIVATION; FLUORINE ION; MG2SIO4; MICROWAVE; POWDERS;

D O I：

10.1016/j.ceramint.2015.07.157

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

In the present work, magnesium orthosilicate powder of high purity and crystallinity was successfully synthesized from precursors of talc and magnesium oxide via solid state reaction through combined steps of 3 h ball mill and annealing at 1400 degrees C for 1 h. The effects of ultrasonication, ball milling and annealing on the mixture of precursors were examined with regards to forsterite (Mg2SiO4) phase formation. Ultrasonication of higher intensity and longer ball mill duration led to reduction in intensity but not total elimination of secondary peaks of enstatite and MgO in the powder. Sintering properties were compared for magnesium orthosilicate prepared from two methods i.e. powder mixture which was ball mill for 3 h and annealed at 1400 degrees C (Type 1) with that which was ball mill for 3 h only (Type 2). It was found that the Type 2 powder exhibited superior densification rate as well as remarkable high hardness (7.7 GPa) and fracture toughness (5.16 MPa m(1/2)) when compared to the Type 1 sintered samples. Despite achieving poorer density, the Type 1 samples exhibited higher elastic modulus without incurring any significant grain growth. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

引用

页码：13614 / 13623

页数：10

共 26 条

[1] Production of forsterite powder using sol-gel technology [J].

Afonina, GA ;

Leonov, VG ;

Popova, ON .

GLASS AND CERAMICS, 2005, 62 (7-8) :248-252

[2] Forsterite ceramics based on sol-gel powders [J].

Andrianov, NT ;

Strel'nikova, SS ;

Dyagilets, SM .

GLASS AND CERAMICS, 2004, 61 (1-2) :16-18

[3] A study of synthetic forsterite refractory materials using waste serpentine cutting [J].

Cheng, TW ;

Ding, YC ;

Chiu, JP .

MINERALS ENGINEERING, 2002, 15 (04) :271-275

[4]

Dorozhkin Sergey V, 2011, Biomatter, V1, P3, DOI 10.4161/biom.1.1.16782

[5] Aqueous syntheses of forsterite (Mg2SiO4) and enstatite (MgSiO3) [J].

Douy, A .

JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2002, 24 (03) :221-228

[6]

Emadi R, 2011, J CERAM PROCESS RES, V12, P538

[7] The effect of fluorine ion on fabrication of nanostructure forsterite during mechanochemical synthesis [J].

Fathi, M. H. ;

Kharaziha, M. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 472 (1-2) :540-545

[8] Novel fabrication of forsterite scaffold with improved mechanical properties [J].

Ghomi, H. ;

Jaberzadeh, M. ;

Fathi, M. H. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (05) :L63-L68

[9] Enstatite based ceramics for machinable prosthesis applications [J].

Goeuriot, D ;

Dubois, JC ;

Merle, D ;

Thevenot, F ;

Exbrayat, P .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1998, 18 (14) :2045-2056

[10] Olivine and forsterite refractories in Europe [J].

Goldschmidt, VM .

INDUSTRIAL AND ENGINEERING CHEMISTRY, 1938, 30 :32-34

← 1 2 3 →