Split-Hopkinson Pressure Bar Test of Silicone Rubber: Considering Effects of Strain Rate and Temperature

被引：5

作者：

Zhu, Xintao ^{[1
]}

Zhang, Xiaojing ^{[1
]}

Yao, Wenjin ^{[1
]}

Li, Wenbin ^{[1
]}

机构：

[1] Nanjing Univ Sci & Technol, ZNDY Ministerial Key Lab, Nanjing 210094, Peoples R China

来源：

POLYMERS | 2022年 / 14卷 / 18期

关键词：

silicone rubber; split-Hopkinson pressure bar; strain rate; temperature; differential scanning calorimetry; DYNAMIC DEFORMATION-BEHAVIOR;

D O I：

10.3390/polym14183892

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Using a split-Hopkinson pressure bar test instrument with a temperature control device, in this work, silicone rubber was tested at different temperatures (-40 degrees C-200 degrees C) and different strain rates (1.2 x 10(3) s(-1)-7.2 x 10(3) s(-1)). The results showed that the dynamic mechanical properties of silicone rubber were strain-rate sensitive at different temperatures and the yield strength of the silicone rubber increased with an increase in the strain rate. At a higher strain rate, silicone rubber showed temperature sensitivity. With a decrease in the strain rate, the influence of temperature on silicone rubber gradually decreased. Differential scanning calorimetry analysis showed that silicone rubber had good thermal stability at high temperatures. When the temperature was as low as -40 degrees C, the silicone rubber underwent a glass transition, showing the characteristics of brittle materials.

引用

页数：12

共 50 条

[11] A Method of Restraining the Geometric Dispersion Effect on Split-Hopkinson Pressure Bar by the Modified Striker Bar [J].

Zou, G. P. ;

Shen, X. H. ;

Chang, Z. L. ;

Wang, Y. W. ;

Wang, P. .

EXPERIMENTAL TECHNIQUES, 2016, 40 (04) :1249-1261

[12] The use of the split Hopkinson pressure bar techniques in high strain rate materials testing [J].

AlMousawi, MM ;

Reid, SR ;

Deans, WF .

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 1997, 211 (04) :273-292

[13] Adaptation of impactor for the split Hopkinson pressure bar in characterizing concrete at medium strain rate [J].

Zhao, PJ ;

Lok, TS .

STRUCTURAL ENGINEERING AND MECHANICS, 2005, 19 (06) :603-618

[14] Pure rate effect on the concrete compressive strength in the split Hopkinson pressure bar test [J].

Lee, Sangho ;

Kim, Kyoung-Min ;

Park, Jamin ;

Cho, Jae-Yeol .

INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2018, 113 :191-202

[15] Application of Split Hopkinson Pressure Bar Test Setup for Determination of Fracture Toughness KC at High Strain Rate Loading [J].

S. Sharma ;

M. K. Samal .

Transactions of the Indian National Academy of Engineering, 2022, 7 (2) :457-461

[16] Dynamic Compressive and Tensile Characterisation of Igneous Rocks Using Split-Hopkinson Pressure Bar and Digital Image Correlation [J].

Wessling, Albin ;

Kajberg, Jorgen .

MATERIALS, 2022, 15 (22)

[17] High-Temperature Split-Hopkinson Pressure Bar with a Momentum Trap for Obtaining Flow Stress Behaviour and Dynamic Recrystallisation [J].

Kajberg, J. ;

Sundin, K. G. .

STRAIN, 2014, 50 (06) :547-554

[18] Design and Calibration of a Large-Scale 155-mm Split-Hopkinson Pressure Bar [J].

Xiong, Beibei ;

Wang, Junsong ;

Benidir, Adel ;

Demartino, Cristoforo ;

Xiao, Yan .

JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2024, 36 (03)

[19] Data-driven parametric modelling of split-Hopkinson pressure bar tests on cohesive soils [J].

Van Lerberghe, Arthur ;

Pasquale, Angelo ;

Rodriguez, Sebastian ;

Barr, Andrew D. ;

Clarke, Sam D. ;

Baillargeat, Dominique ;

Chinesta, Francisco .

INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2025, 198

[20] THICKNESS EFFECTS IN SPLIT HOPKINSON PRESSURE BAR TESTS [J].

DIOH, NN ;

LEEVERS, PS ;

WILLIAMS, JG .

POLYMER, 1993, 34 (20) :4230-4234

← 1 2 3 4 5 →