Effects of water vapor on corrosion behaviors of C/SiC in oxidizing atmosphere containing Na2SO4 vapor

被引：13
|
作者：
Luan, Xin'gang [1 ]
Zhang, Jun [1 ]
Cheng, Laifei [1 ]
机构：
[1] NW Polytech Univ, Sci & Technol Thermlstruct Composite Mat Lab, Xian 710072, Shaanxi, Peoples R China
来源：
COMPOSITES PART B-ENGINEERING | 2012年 / 43卷 / 08期
关键词：
Ceramic-matrix composites (CMCs); Corrosion; Damage mechanics; Electron microscopy; SIO2 SCALE VOLATILITY; SILICON-BASED CERAMICS; COMBUSTION CONDITIONS; SALT VAPOR; ENVIRONMENTS; OXIDATION; COMPOSITE; RECESSION; KINETICS; CARBIDE;
D O I：
10.1016/j.compositesb.2012.05.047
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion of a C/SiC composite has been investigated in the atmosphere containing oxygen, water vapor and sodium sulfate vapor at the temperatures range from 1000 to 1500 degrees C. The effect of water vapor on the corrosion mechanism of C/SiC were discussed based on the weight change, the residual strength change, the microstructure and calculated results from FactSage. The corrosion of C/SiC is attributed to (i) the permeation of gas through the SiO2 film below 1300 degrees C, (ii) the diffusion of oxidant through pores caused by bubbles broken in the SiO2 film above 1300 degrees C. The water vapor does not change the corrosion mechanism of C/SiC composite but the temperature range in which the corrosion mechanism works by accelerating the oxidation of SIC and the corrosion of SiO2. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2968 / 2972
页数：5
相关论文
共 50 条
  • [41] The role of the conversion reactions of NaCl to Na2SO4 and KCl to K2SO4 in reducing of boiler superheaters corrosion
    Waclawiak, Krzysztof
    Tomeczek, Jerzy
    Gradon, Boguslaw
    OCHRONA PRZED KOROZJA, 2014, 57 (11): : 422 - 426
  • [42] Corrosion processes of Mg-Y-Nd-Zr alloys in Na2SO4 electrolyte
    Ardelean, H.
    Seyeux, A.
    Zanna, S.
    Prima, F.
    Frateur, I.
    Marcus, P.
    CORROSION SCIENCE, 2013, 73 : 196 - 207
  • [43] Hot corrosion and protection of Ti2AlC against Na2SO4 salt in air
    Lin, Zhijun
    Zhou, Yanchun
    Li, Meishuan
    Wang, Jingyang
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (16) : 3871 - 3879
  • [44] A kinetic model of the spontaneous passivation and corrosion of zinc in near neutral Na2SO4 solutions
    Sziraki, L
    Cziraki, A
    Gerocs, I
    Vertesy, Z
    Kiss, L
    ELECTROCHIMICA ACTA, 1998, 43 (1-2) : 175 - 186
  • [45] Hot corrosion of the Ni-20%Cr alloy and waspaloy immersed in Na2SO4
    Kusabiraki, Kiyoshi
    Morita, Masashi
    Guo, Xiping
    Anada, Hiroshi
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2007, 93 (07): : 498 - 505
  • [46] Hot corrosion behaviour of barium-strontium aluminosilicates in a molten Na2SO4 environment
    Jiang, Fengrui
    Cheng, Laifei
    Wang, Yiguang
    Huang, Xuanxuan
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (02) : 823 - 832
  • [47] Hot Corrosion of T22, T23, and T91 Steels in Na2SO4 Salts at 800 and 900 °C
    Kim, Seul Ki
    Xu, Chunyu
    Hwang, Yeon Sang
    Lee, Dong Sok
    KOREAN JOURNAL OF METALS AND MATERIALS, 2013, 51 (12): : 849 - 856
  • [48] Mechanical Properties and Oxidation Behaviors of Self-Healing SiCf/SiC-SiBCN Composites Exposed to H2O/O2/Na2SO4 Environments
    Ji, Suya
    Liang, Bin
    Hu, Chenglong
    Pang, Shengyang
    Zhao, Rida
    Li, Jian
    Tang, Sufang
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (11) : 1909 - 1923
  • [49] Early Strength Evolution of Cement Grouts Adopted in Reinforced Concrete Subjected to Na2SO4 Corrosion
    Xu, Yinshan
    Zhou, Jianqiang
    Jin, Sujing
    BUILDINGS, 2023, 13 (03)
  • [50] A study on corrosion mechanism of 15CrMo in saline (Na2SO4) steam at high temperature
    Bai, Bing
    Deng, Lei
    Che, Defu
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (06): : 971 - 979
12345