The Effect of Titanium Carbonitride on the Viscosity of High-Titanium-Type Blast Furnace Slag

被引:13
作者
Xie, Hongen [1 ,2 ]
Yu, Wenzhou [1 ,3 ]
You, Zhixiong [1 ,3 ]
Lv, Xuewei [1 ,3 ]
Bai, Chenguang [3 ]
机构
[1] Chongqing Univ, Coll Mat Sci & Engn, Chongqing 400045, Peoples R China
[2] Pangang Grp Res Inst Co Ltd, State Key Lab Vanadium & Titanium Resources Compr, Panzhihua 617000, Peoples R China
[3] Chongqing Univ, Chongqing Key Lab Vanadium Titanium Met & Adv Mat, Chongqing 400044, Peoples R China
来源
METALS | 2019年 / 9卷 / 04期
基金
中国国家自然科学基金;
关键词
blast furnace slag; TiO2; titanium carbonitride; viscosity; TIO2; BEHAVIOR;
D O I
10.3390/met9040395
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this paper, the effect of titanium carbonitride (Ti(C,N)) on the viscosity of high-titanium-type blast furnace slags was investigated. The different Ti(C,N) contents were achieved by adjusting the reduction degree of TiO2 to reflect the real characteristics of the high-titanium slag. The results show that the viscosity of the slag increased with the increasing Ti(C,N) content and decreased with the rising temperature. A deviation between the measured and the fitted viscosity appeared as the content of the Ti(C,N) was beyond 4 wt%. Furthermore, the apparent viscous flow activation energy of the slag ranged from 106.13 kJ/mol to 235.46 kJ/mol by varying the Ti(C,N) contents from 0 wt% to 4.97 wt%, which was evidently different from the results of previous studies. The optical microscope and energy dispersive X-ray spectroscopy (EDS) analysis show that numerous bubble cavities were embedded in the slags and the Ti(C,N) particles agglomerated in the solidified samples. This phenomenon further indicates that the high-titanium slag is a polyphase dispersion system, which consists of liquid slag, solid Ti(C,N) particles and bubbles.
引用
收藏
页数:10
相关论文
共 22 条
[1]  
EINSTEIN A, 1959, INVESTIGATIONS THEOR
[2]   Influence of B2O3 and TiO2 on Viscosity of Titanium-Bearing Blast Furnace Slag [J].
Gao, Yanhong ;
Bian, Lingtao ;
Liang, Zhongyu .
STEEL RESEARCH INTERNATIONAL, 2015, 86 (04) :386-390
[3]   Viscosity of TiO2-FeO-Ti2O3-SiO2-MgO-CaO-Al2O3 for High-Titania Slag Smelting Process [J].
Hu, Kai ;
Lv, Xuewei ;
Li, Shengping ;
Lv, Wei ;
Song, Bing ;
Han, Kexi .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2018, 49 (04) :1963-1973
[4]   SLAG FOAMING IN BATH SMELTING [J].
JIANG, R ;
FRUEHAN, RJ .
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1991, 22 (04) :481-489
[5]   Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag [J].
Jiang, Tao ;
Liao, De-ming ;
Zhou, Mi ;
Zhang, Qiao-yi ;
Yue, Hong-rui ;
Yang, Song-tao ;
Duan, Pei-ning ;
Xue, Xiang-xin .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2015, 22 (08) :804-810
[6]   Influence of TiO2 and basicity on viscosity of Ti bearing slag [J].
Liao, J. L. ;
Li, J. ;
Wang, X. D. ;
Zhang, Z. T. .
IRONMAKING & STEELMAKING, 2012, 39 (02) :133-139
[7]   Influence of Ti(C0.3N0.7) on viscosity of blast furnace slags [J].
Liu, Y. -X. ;
Zhang, J. -L. ;
Zhang, G. -H. ;
Jiao, K. -X. ;
Chou, K. -C. .
IRONMAKING & STEELMAKING, 2017, 44 (08) :609-618
[8]   Thermodynamics of TiO2 in blast furnace-type slags [J].
Morizane, Y ;
Ozturk, B ;
Fruehan, RJ .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1999, 30 (01) :29-43
[9]   Effect of TiO2 on the Viscosity and Slag Structure in Blast Furnace Type Slags [J].
Park, Hyunsik ;
Park, Jun-Young ;
Kim, Gi Hyun ;
Sohn, Il .
STEEL RESEARCH INTERNATIONAL, 2012, 83 (02) :150-156
[10]   THE VISCOSITY OF SUSPENSIONS OF RIGID SPHERES [J].
ROSCOE, R .
BRITISH JOURNAL OF APPLIED PHYSICS, 1952, 3 (AUG) :267-269