L10-FePt films fabricated by wet-chemical route

被引：1

作者：

Hong, Xiaoliang ^{[1
]}

Xiao, Wen ^{[1
]}

Bao, Nina ^{[1
]}

Li, Weimin ^{[1
]}

Chichvarina, Olga ^{[1
]}

Ding, Jun ^{[1
]}

机构：

[1] Natl Univ Singapore, Dept Mat Sci & Engn, Singapore 119260, Singapore

来源：

THIN SOLID FILMS | 2015年 / 589卷

关键词：

Iron-platinum; Iron; Thin films; Chemical deposition; Post-annealing treatment; Perpendicular anisotropy; FEPT THIN-FILMS; MAGNETIC-PROPERTIES; PERPENDICULAR ANISOTROPY; TEMPERATURE; DEPOSITION; NANOPARTICLES; AL2O3;

D O I：

10.1016/j.tsf.2015.06.051

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, we have developed a method to fabricate FePt films by a combination of chemical deposition and post-annealing. Pt-doped Fe films were deposited on Pt(100 nm)/Ti(50 nm)/SiO2/Si substrate using thermal deposition and the as-deposited films were subsequently annealed from 300 degrees C to 800 degrees C under 5% H-2/95% N-2. FePt films were achieved through diffusion and rearrangement of Fe and Pt atoms in post-annealing process. From X-ray diffraction results, the face-centered cubic (fcc) FePt phase appeared at 300 degrees C and the transformation from fcc to L10 phase started at 400 degrees C. The L1(0)-FePt film possessed an out-of-plane anisotropy and a coercivity of 729 kA/m after annealing at 600 degrees C. A further increase in annealing temperature led to lower value of coercivity, probably because of grain growth. In addition, the thickness of Pt-doped Fe films could be controlled from 150 nm to 700 nm by adjusting the amount of surfactant used. Our superconducting quantum interference device analysis showed that Pt dopant could significantly improve the chemical stability of Fe films in air. (C) 2015 Elsevier B.V. All rights reserved.

引用

页码：649 / 654

页数：6

共 39 条

[11] Ferromagnetic FePt nanowires: Solvothermal reduction synthesis and characterization [J].

Hou, YL ;

Kondoh, H ;

Che, RC ;

Takeguchi, M ;

Ohta, T .

SMALL, 2006, 2 (02) :235-238

[12] Effect of Pt underlayer on the coercivity of FePt sputtered film [J].

Hsu, C. W. ;

Chen, S. K. ;

Liao, W. M. ;

Yuan, F. T. ;

Chang, W. C. ;

Tsai, J. L. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 449 (1-2) :52-55

[13] In situ ordering of FePt thin films by using Ag/Si and Ag/Mn3Si/Ag/Si templates [J].

Hsu, YN ;

Jeong, S ;

Lambeth, DN ;

Laughlin, DE .

IEEE TRANSACTIONS ON MAGNETICS, 2000, 36 (05) :2945-2947

[14]

IVANOV OA, 1973, FIZ MET METALLOVED+, V35, P92

[15] Polymer-assisted deposition of metal-oxide films [J].

Jia, QX ;

Mccleskey, TM ;

Burrell, AK ;

Lin, Y ;

Collis, GE ;

Wang, H ;

Li, ADQ ;

Foltyn, SR .

NATURE MATERIALS, 2004, 3 (08) :529-532

[16] Thickness dependence of (001) texture evolution in FePt thin films on an amorphous substrate [J].

Kim, Jae-Song ;

Koo, Yang-Mo .

THIN SOLID FILMS, 2008, 516 (06) :1147-1154

[17] Perpendicular anisotropy of MBE-grown FePt-Ag granular films [J].

Konagai, T. ;

Kitahara, Y. ;

Itoh, T. ;

Kato, T. ;

Iwata, S. ;

Tsunashima, S. .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 310 (02) :2662-2664

[18] Synthesis of phase pure iron oxide polymorphs thin films and their enhanced magnetic properties [J].

Kumar, Pawan ;

No-Lee, Heung ;

Kumar, Rajesh .

JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2014, 25 (10) :4553-4561

[19] Highly coercive electrodeposited FePt films by postannealing in hydrogen [J].

Leistner, K ;

Thomas, J ;

Schlörb, H ;

Weisheit, M ;

Schultz, L ;

Fähler, S .

APPLIED PHYSICS LETTERS, 2004, 85 (16) :3498-3500

[20] Patterning of FePt for magnetic recording [J].

Li, G. J. ;

Leung, C. W. ;

Lei, Z. Q. ;

Lin, K. W. ;

Lai, P. T. ;

Pong, Philip W. T. .

THIN SOLID FILMS, 2011, 519 (23) :8307-8311

← 1 2 3 4 →