Investigating the effect of Cd-Mn co-doped nano-sized BiFeO3 on its physical properties

This work deals with the investigation of different effects on the structural, magnetic, electronic and dielectric properties of Cd and Mn doped Bi0.75Cd0.25Fe1-xMnxO3 multiferroic samples by taking fixed ratios of Cd and varying the Mn ratio with values of x = 0.0, 0.5, 0.10 and 0.15. Cd-Mn doped samples were synthesized chemically using a microemulsion method. All the samples were finally sintered at 700 degrees C for 2 h to obtain the single phase perovskites structure of BiFeO3 materials. The synthesized samples were characterized by different techniques, such as X-ray diffractometry (XRD), Scanning Electron Microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), LCR meter and magnetic properties using VSM. XRD results confirm BFO is a perovskite structure having crystallite size in the range of 24-54 nm. XRD results also reveal observed structural distortion due to doping of Cd at the A-site and Mn at the B-site of BFO. SEM results depict that, as the substitution of Cd-Mn increases in BFO, grain size decreases up to 30 nm. FTIR spectra showed prominent absorption bands at 555 cm (1) and 445 cm (1) corresponding to the stretching vibrations of the metal ions complexes at site A and site B, respectively. Variation of dielectric constant (epsilon') and loss tangent (tan delta) at room temperature in the range of 1 MHz to 3 GHz have been investigated. Results reveal that with Cd-Mn co doping a slight decrease in dielectric constant have been observed. Magnetic properties of Cd-Mn doped pure BFO samples have been studied at 300 K. Results reveal that undoped BiFeO3 exhibits weak ferromagnetic ordering due to the canting of its spin. Increase in magnetization and decrease in coercivity is a clear indication that a material can be used in high density recording media and memory devices. (C) 2016 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).