Iron reduction in aluminum by electroslag refining

被引：3

作者：

Chen Chong ^{[1
]}

Wang Jun ^{[1
]}

Shu Da ^{[1
]}

Xue Jing ^{[1
]}

Sun Bao-de ^{[1
]}

Xue Yong-sheng ^{[2
]}

Yan Qing-min ^{[2
]}

机构：

[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, State Key Lab Met Matrix Composites, Shanghai 200240, Peoples R China

[2] Suzhou Zhenwu Elect Furnace Co Ltd, Suzhou 215168, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2012年 / 22卷 / 04期

基金：

中国国家自然科学基金;

关键词：

aluminum; electroslag refining; iron; mechanical properties; thermodynamic calculation; INTERMETALLIC COMPOUNDS; ALLOYS; FE; TITANIUM; SYSTEM; CORNER;

D O I：

10.1016/S1003-6326(11)61271-5

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effect of electroslag refining on iron reduction from commercial aluminum was investigated. Cast electrodes of commercial aluminum were electroslag refined using KCl-NaCl-Na3AlF6 slag containing Na2B4O7. Experimental results indicate that the iron content decreases with increasing Na2B4O7 addition and remelting time, and the iron content decreases from 0.400% to 0.184% under 9% Na2B4O7 addition for 30 min remelting. The elastic modulus, yield strength and ultimate tensile strength commercial aluminum are improved, and the tensile elongation is increased by 43% after electroslag refining. The chemical reaction between melt and slag to form Fe2B is the main reason for iron reduction and the thermodynamic calculation of the chemical reaction theoretically accounts for the formation of Fe2B.

引用

页码：964 / 969

页数：6

共 19 条

[1] Intermetallic phase selection in 1XXX Al alloys [J].

Allen, CM ;

O'Reilly, KAQ ;

Cantor, B ;

Evans, PV .

PROGRESS IN MATERIALS SCIENCE, 1998, 43 (02) :89-170

[2] The solidification characteristics of Fe-rich intermetallics in Al-11.5Si-0.4Mg cast alloys [J].

Cao, X ;

Campbell, J .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (05) :1425-1435

[3] An isothermal section at 550 degrees C in the Al-rich corner of the Al-Fe-Mn-Si system [J].

Davignon, G ;

Serneels, A ;

Verlinden, B ;

Delaey, L .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (11) :3357-3361

[4] Removal of iron from molten recycled aluminum through intermediate phase filtration [J].

de Moraes, Humberto Lopes ;

de Oliveira, Jose Roberto ;

Romano Espinosa, Denise Crocce ;

Soares Tenorio, Jorge Alberto .

MATERIALS TRANSACTIONS, 2006, 47 (07) :1731-1736

[5]

DUCKWORTH WE, 1969, ELECTROSLAG REFINING, P7

[6] A kinetic study on the nucleation and growth of the Al8FeMnSi2 intermetallic compound for aluminum scrap purification [J].

Flores, A ;

Sukiennik, M ;

Castillejos, AH ;

Acosta, FA ;

Escobedo, JC .

INTERMETALLICS, 1998, 6 (03) :217-227

[7] Effects of Na2B4O7 on the elimination of iron from aluminum melt [J].

Gao, J. W. ;

Shu, D. ;

Wang, J. ;

Sun, B. D. .

SCRIPTA MATERIALIA, 2007, 57 (03) :197-200

[8] Effect of Ce and La on microstructure and properties of a 6xxx series type aluminum alloy [J].

Hosseinifar, Mehdi ;

Malakhov, Dmitri V. .

JOURNAL OF MATERIALS SCIENCE, 2008, 43 (22) :7157-7164

[9]

HU Jian-hua, 2002, PRACTICAL INORGANIC, P57

[10] Iron intermetallic phases in the Al corner of the Al-Si-Fe system [J].

W. Khalifa ;

F. H. Samuel ;

J. E. Gruzleski .

Metallurgical and Materials Transactions A, 2003, 34 (3) :807-825

← 1 2 →