Naproxen-Based Hydrazones as Effective Corrosion Inhibitors for Mild Steel in 1.0 M HCl

The corrosion-inhibiting performance of (E)-N'-(4-bromobenzylidene)-2-(6-methoxynaphthalen-2-yl) propanehydrazide (BPH) and (E)-N'-(4-(dimethylamino) benzylidene)-2-(6-methoxynaphthalen-2-yl) propanehydrazide (MPH) for mild steel (MS) in 1.0 M HCl was investigated using electrochemical methods, weight loss measurements, and scanning electron microscope (SEM) coupled with energy dispersive X-ray spectroscope (EDX) analysis. Raising the concentration of both inhibitors towards an optimal value of 5 x 10(-3)M reduced the corrosion current density (i(corr)) and the corrosion rate of mild steel. The inhibitory effect of MPH, which showed the highest inhibition efficiency, was explored under a range of temperatures between 303 and 333 K. The inhibitory performance of both compounds significantly improved when the inhibitor concentration increased. The main result that flowed from potentiodynamic polarization (PDP) tests was that both compounds acted as mixed-type inhibitors, with a predominance cathodic effect. The adsorption of both compounds follows the Langmuir isotherm. SEM/EDX confirmed the excellent inhibition performance of tested compounds.