Effect of loading bimetallic mixture of Ni and Pd on hydrogen storage capacity of MCM-41

MCM-41 was produced by microwave irradiation, which allows high yield, improved product purity, increased reaction rate and crystallization. As transition metals enhance the hydrogen uptake, Pd and Ni were loaded on MCM-41 to increase the hydrogen storage capacity of the structure. The surface areas of the samples were measured by N-2 adsorption and it was observed that they had large surface area around 938-1369 m(2)/g. The successful incorporation of metals into the structure was confirmed by characterization using X-ray diffraction and X-ray photoelectron spectroscopy. The hydrogen adsorption capacities of the samples were measured by the Intelligent Gravimetric Analyzer at room temperature and up to 10 bar pressure. The hydrogen storage capacity of MCM-41 was improved by increasing content of bimetallic mixture of Pd and Ni. The maximum hydrogen uptake was obtained as 0.98 wt% with 10:100 Pd Ni:MCM-41. Copyright (c) 2015, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.