Failure analysis of H13 steel die for high pressure die casting Al alloy

被引：38

作者：

Ding, Rengen ^{[1
]}

Yang, Haibo ^{[1
]}

Li, Shuzhi ^{[1
]}

Hu, Guodong ^{[1
]}

Mo, Jiahao ^{[1
]}

Chu, Mingqiang ^{[1
]}

Paddea, Sanjoo ^{[1
]}

Zhang, Shuyan ^{[1
]}

Zhang, Peng ^{[1
]}

Liu, Zhongren ^{[2
]}

Wei, Junjun ^{[2
]}

机构：

[1] Ctr Excellence Adv Mat, Dongguan, Peoples R China

[2] Silver Basis Technol Co LTD, Shenzhen, Guangdong, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2021年 / 124卷

关键词：

Failure analysis; H13; steel; Die; Residual stress; Electron microscopy;

D O I：

10.1016/j.engfailanal.2021.105330

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

High pressure die casting (HPDC) die is operated at severe conditions such as high pressure, high temperature and corrosion, which limit its service life. Analysis of failure mechanism of the die is beneficial to guide die design and choose of materials so as to improve the die life. A failed H13 steel die which was used to manufacture a 5G component via Al alloy HPDC, has been investigated using a complementary range of techniques such as X-ray diffractometer (XRD), Optical microscopy (OM), Scanning electron microscopy (SEM), and Transmission electron microscopy (TEM). The results show that erosion and cracking are two main failure modes. Furthermore, the fatal cracking occurs around fillet radius and hole/insert, which is correlated with high local stresses.

引用

页数：13

共 23 条

[1] Adler WF., 1979, Erosion, V16, P127
[2] Die erosion and its effect on soldering formation in high pressure die casting of aluminium alloys
Chen, ZW
Jahedi, MZ
[J]. MATERIALS & DESIGN, 1999, 20 (06): : 303 - 309
[3] Heat treatment and properties of a hot work tool steel fabricated by additive manufacturing
Deirmina, Faraz
Peghini, Nicola
AlMangour, Bandar
Grzesiak, Dariusz
Pellizzari, Massimo
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 753 (109-121): : 109 - 121
[4] Modeling of high temperature- and diffusion-controlled die soldering in aluminum high pressure die casting
Domkin, K.
Hattel, J. H.
Thorborg, J.
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (08) : 4051 - 4061
[5] Heymann F., 1992, ASM Handbook, V18, P221
[6] Erosion process analysis of die-casting inserts for magnesium alloy components
Hou, Li-feng
Wei, Ying-hui
Li, Yong-gang
Liu, Bao-sheng
Du, Hua-yun
Guo, Chun-li
[J]. ENGINEERING FAILURE ANALYSIS, 2013, 33 : 457 - 464
[7] Failure analysis of an open die forging drop hammer
Irisarri, A. M.
Pelayo, A.
[J]. ENGINEERING FAILURE ANALYSIS, 2009, 16 (05) : 1727 - 1733
[8] Causes of failure and repairing options for dies and molds: A review
Jhavar, S.
Paul, C. P.
Jain, N. K.
[J]. ENGINEERING FAILURE ANALYSIS, 2013, 34 : 519 - 535
[9] Dissolution and soldering behavior of nitrided hot working steel with multilayer LAFAD PVD coatings
Joshi, V
Kulkarni, K
Shivpuri, R
Bhattacharya, RS
Dikshit, SJ
Bhat, D
[J]. SURFACE & COATINGS TECHNOLOGY, 2001, 146 : 338 - 343
[10] Failure mechanisms of H13 die on relation to the forging process - A case study of brass gas valves
Kchaou, Mohamed
Elleuch, Riadh
Desplanques, Yannick
Boidin, Xavier
Degallaix, Gerard
[J]. ENGINEERING FAILURE ANALYSIS, 2010, 17 (02) : 403 - 415

← 1 2 3 →