Flexural strength of zirconia/stainless steel functionally graded materials

被引：1

作者：

Li Jun ^{[1
]}

Zhao Kang ^{[1
]}

Tang Yu-fei ^{[1
]}

Li Da-yu ^{[1
]}

机构：

[1] Xian Univ Technol, Sch Mat & Engn, Xian 710048, Peoples R China

来源：

JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY | 2009年 / 16卷 / 06期

关键词：

ZrO2; functionally graded materials; flexural strength; fracture; tape casting; COMPOSITES; FRACTURE; ARMOR;

D O I：

10.1007/s11771-009-0148-6

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Zirconia/stainless steel (ZrO2/SUS316L) functionally graded materials (FGMs) were fabricated by tape casting and laminating. Microstructures of FGMs were observed by optical microscope. Fracture behavior of FGMs in different loading modes and influences of different gradient changes on flexural strength were investigated. The results show that ZrO2/ SUS316L FGMs with graded components at interlayers are obtained after they are sintered in vacuum and pressureless condition at 1 350 A degrees C. The I-II mixed mode crack creates in composite layer and grows to both sides zigzag while loading on ZrO2 layer. Flexural strengths are 496.4, 421.7 and 387.5 MPa when gradient changes are 10%, 15% and 20%, but flexural strengths of the corresponding fracture layers are 387.1, 334.6 and 282.3 MPa since cracks of FGMs are affected by three-dimensional stress, respectively. The cracks are generated in ZrO2 layer and extend to SUS316L layer while loading is added on SUS316L layer, flexural strength does not change with the graded components and keeps consistent basically.

引用

页码：892 / 896

页数：5

共 20 条

[1] Interaction integrals for thermal fracture of functionally graded materials [J].

Amit, K. C. ;

Kim, Jeong-Ho .

ENGINEERING FRACTURE MECHANICS, 2008, 75 (08) :2542-2565

[2]

ANNIKA P, 2005, INT J IMPACT ENG, V32, P387

[3] Fracture analysis of functionally graded materials by a BEM [J].

Gao, X. W. ;

Zhang, Ch. ;

Sladek, J. ;

Sladek, V. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2008, 68 (05) :1209-1215

[4]

[韩辉 HAN Hui], 2007, [材料导报, Materials Review], V21, P34

[5] Synthesis and characterization of Nb5Si3/Nb functionally graded composites [J].

Heian, EM ;

Gibeling, JC ;

Munir, ZA .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 368 (1-2) :168-174

[6] Thermal residual stress analysis of diamond coating on graded cemented carbides [J].

Huang Zi-qian ;

He Yue-hui ;

Cai Hai-tao ;

Wu Cong-hai ;

Xiao Yi-feng ;

Huang Bai-yun .

JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2008, 15 (02) :165-169

[7] Zirconia/stainless-steel continuous functionally graded material [J].

López-Esteban, S ;

Bartolomé, JF ;

Pecharromán, C ;

Moya, JS .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (16) :2799-2804

[8]

LU Y, 2003, ADV COMPOSITES

[9] Preparation of β-Sialon/ZrN bonded corundum composites from zircon by nitridation reaction sintering process [J].

Ma Bei-yue ;

Yu Jing-kun ;

Liu Tao ;

Yan Zheng-guo .

JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2009, 16 (05) :725-729

[10] Recent developments toward the use of tungsten as armour material in plasma facing components [J].

Mitteau, R. ;

Missiaen, J. M. ;

Brustolin, P. ;

Ozer, O. ;

Durocher, A. ;

Ruset, C. ;

Lungu, C. P. ;

Courtois, X. ;

Dominicy, C. ;

Maier, H. ;

Grisolia, C. ;

Piazza, G. ;

Chappulis, P. .

FUSION ENGINEERING AND DESIGN, 2007, 82 (15-24) :1700-1705

← 1 2 →