Leaching, carbonation and chloride ingress in reinforced alkali activated fly ash mortars

被引：4

作者：

Gluth, Gregor J. G. ^{[1
]}

Hlavacek, Petr ^{[1
]}

Reinemann, Steffi ^{[2
]}

Ebell, Gino ^{[2
]}

Mietz, Juergen ^{[2
]}

机构：

[1] Bundesanstalt Mat Forsch & Prufung BAM, 7-4 Technol Construct Mat, D-12205 Berlin, Germany

[2] Bundesanstalt Mat Forsch & Prufung BAM, 7-6 Corros & Corros Protect, D-12205 Berlin, Germany

来源：

INTERNATIONAL CONFERENCE ON CONCRETE REPAIR, REHABILITATION AND RETROFITTING (ICCRRR 2018) | 2018年 / 199卷

关键词：

ACCELERATED CARBONATION; CORROSION BEHAVIOR; PORE SOLUTION; SLAG CEMENT; STEEL BARS; RESISTANCE; DURABILITY; CONCRETE;

D O I：

10.1051/matecconf/201819902025

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Alkali-activated fly ash mortars were studied with regard to durability-relevant transport coefficients and the electrochemical behaviour of embedded carbon steel bars on exposure of the mortars to leaching, carbonation and chloride penetration environments. The transport coefficients differed considerably between different formulations, being lowest for a mortar with BFS addition, but still acceptable for one of the purely fly ash-based mortars. Leaching over a period of similar to 300 days in de-ionized water did not lead to observable corrosion of the embedded steel, as shown by the electrochemical data and visual inspection of the steel. Exposure to 100 % CO2 atmosphere caused steel depassivation within approx. two weeks; in addition, indications of a deterioration of the mortar were observed. The results are discussed in the context of the different reaction products expected in high- and low-Ca alkali-activated binders, and the alterations caused by leaching and carbonation.

引用

页数：7

共 50 条

[31] Steel passive state stability in activated fly ash mortars [J].

Fernandez-Jimenez, A. ;

Miranda, J. M. ;

Gonzalez, J. A. ;

Palomo, A. .

MATERIALES DE CONSTRUCCION, 2010, 60 (300) :51-65

[32] Effect of natural carbonation on the pore structure and elastic modulus of the alkali-activated fly ash and slag pastes [J].

Nedeljkovic, Marija ;

Savija, Branko ;

Zuo, Yibing ;

Lukovic, Mladena ;

Ye, Guang .

CONSTRUCTION AND BUILDING MATERIALS, 2018, 161 :687-704

[33] Effect of curing conditions on the pore solution and carbonation resistance of alkali-activated fly ash and slag pastes [J].

Nedeljkovic, Marija ;

Ghiassi, Bahman ;

van der Laan, Sieger ;

Li, Zhenming ;

Ye, Guang .

CEMENT AND CONCRETE RESEARCH, 2019, 116 :146-158

[34] Corrosion behavior of steel in alkali-activated fly ash mortars in the light of their microstructural, mechanical and chemical characterization [J].

Monticelli, C. ;

Natali, M. E. ;

Balbo, A. ;

Chiavari, C. ;

Zanotto, F. ;

Manzi, S. ;

Bignozzi, M. C. .

CEMENT AND CONCRETE RESEARCH, 2016, 80 :60-68

[35] Effect of Na2O concentration and water/binder ratio on carbonation of alkali-activated slag/fly ash cements [J].

Zhang, Jian ;

Shi, Caijun ;

Zhang, Zuhua .

CONSTRUCTION AND BUILDING MATERIALS, 2021, 269

[36] Microstructural changes in alkali-activated slag mortars induced by accelerated carbonation [J].

Li, Ning ;

Farzadnia, Nima ;

Shi, Caijun .

CEMENT AND CONCRETE RESEARCH, 2017, 100 :214-226

[37] Effect of waste glass powder as a partial precursor in ambient cured alkali activated fly ash and fly ash-GGBFS mortars [J].

Khan, Md Nabi Newaz ;

Kuri, Jhutan Chandra ;

Sarker, Prabir Kumar .

JOURNAL OF BUILDING ENGINEERING, 2021, 34

[38] Effect of fly ash to slag ratio and Na2O content on leaching behaviour of fly Ash/Slag based alkali activated materials [J].

Srinivasamurthy, Lakshmikanth ;

Chevali, Venkata S. ;

Zhang, Zuhua ;

Wang, Hao .

CONSTRUCTION AND BUILDING MATERIALS, 2023, 383

[39] Effect of lime neutralization wastewater on the performance of alkali-activated slag/fly ash mortars [J].

Zhou, Tao ;

Li, Jin .

MATERIALS AND STRUCTURES, 2024, 57 (09)

[40] Alkali cation effects on chloride binding of alkali-activated fly ash and metakaolin geopolymers [J].

Fu, Chuanqing ;

Ye, Hailong ;

Zhu, Kaiqi ;

Fang, Deming ;

Zhou, Jianbo .

CEMENT & CONCRETE COMPOSITES, 2020, 114

← 1 2 3 4 5 →