Analysis of fatigue failure of drill pipe in air drilling

被引：0
|
作者：
Zhao Guanghui [1 ]
Liang Zheng [1 ]
机构：
[1] SWPU, Sch Mechatron Engn, Chengdu 610500, Peoples R China
来源：
ENGINEERING STRUCTURAL INTEGRITY: RESEARCH, DEVELOPMENT AND APPLICATION, VOLS 1 AND 2 | 2007年
关键词：
D O I：
暂无
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
On the basis of the working condition of Puguang gas field in Sichuan province of China, dynamic analysis of the drill pipes (DP) near the bottom-hole assembly (BHA) in air drilling and prediction of fatigue life were carried out roundly. Influence of the drilling parameters on the DP's fatigue life was presented. It's found that the bending wave caused by backward precession of BHA has a main effect on the DP's fatigue fracture. Small increasing of torque on bit JOB) shortens fatigue life greatly. Higher speed of rotation (SOR) corresponds to shorter fatigue life for it aggravating axial and transverse vibration. Increasing weight on bit (WOB) reduces fatigue life due to decreasing tension of DP, increasing transverse vibration and TOB.
引用
收藏
页码：411 / 413
页数：3
相关论文
共 50 条
  • [21] Analysis of failure causes of S135 drill pipe
    Spasova, Daniela
    Argirov, Yaroslav
    Atanasov, Nikolay
    Yankova, Radostina
    MATERIALS TODAY-PROCEEDINGS, 2022, 59 : 1719 - 1725
  • [22] Failure Analysis on Fracture of a S135 Drill Pipe
    Han Yan
    Zhao Xuehu
    Bai Zhenquan
    Yin Chengxian
    20TH EUROPEAN CONFERENCE ON FRACTURE, 2014, 3 : 447 - 453
  • [23] Corrosion Failure Analysis of a S135 Drill Pipe
    Jinlan Zhao
    Xiaoliang Bai
    Tingting Qu
    Dongfeng Li
    Wenhong Liu
    Zunyi Wei
    Li Xiaolong
    Journal of Failure Analysis and Prevention, 2024, 24 : 368 - 379
  • [24] Corrosion Failure Analysis of a S135 Drill Pipe
    Zhao, Jinlan
    Bai, Xiaoliang
    Qu, Tingting
    Li, Dongfeng
    Liu, Wenhong
    Wei, Zunyi
    Li, Xiaolong
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2024, 24 (01) : 368 - 379
  • [25] Analysis of fatigue behaviour of drill pipe on pin-box connection
    Ozguc, Ozgur
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART M-JOURNAL OF ENGINEERING FOR THE MARITIME ENVIRONMENT, 2021, 235 (01) : 68 - 80
  • [26] Stress intensity factors and fatigue growth of a surface crack in a drill pipe during rotary drilling operation
    Ngoc Ha Dao
    Sellami, Hedi
    ENGINEERING FRACTURE MECHANICS, 2012, 96 : 626 - 640
  • [27] EVALUATION OF METHODS TO ALLEVIATE CORROSION FATIGUE IN TYPE 135 DRILL PIPE STEEL FOR OFFSHORE DRILLING APPLICATIONS
    PETTIT, DE
    HOEPPNER, DW
    HYLER, WS
    MATERIALS RESEARCH AND STANDARDS, 1968, 8 (08): : 34 - &
  • [28] DRILL PIPE JOINTS WEAR UNDER ROTOR DRILLING
    YALALDINOV, RA
    AIZUPPE, EA
    KABISHCHER, LL
    NEFTYANOE KHOZYAISTVO, 1990, (05): : 20 - 25
  • [29] Drill pipe corrosion fatigue life prediction by using failure assessment diagram technique
    Zhang, PS
    Han, XY
    Luo, WG
    Han, XL
    Li, HL
    FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2293 - 2298
  • [30] Drill pipe and muds - important aspects in drilling technology
    Griffin, Jeff
    No-Dig International, 1996, 7 (04):
12345