Analysis of distillation plant stainless steel corrosion behavior

被引：0
作者：
Wang, Xiaojing [1 ]
Gao, Weidong [1 ]
机构：
[1] Tianjin Univ, Inst Chem Technol, Tianjin 300072, Peoples R China
来源：
ADVANCED COMPOSITE MATERIALS, PTS 1-3 | 2012年 / 482-484卷
关键词：
stainless steel; stress corrosion; tubes: cracking; FAILURE ANALYSIS;
D O I：
10.4028/www.scientific.net/AMR.482-484.1290
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
In tar distillation plant of the stainless steel plate tower wall's corrosion and heat exchanger tubes' cracking fracture were analyzed, including the microstructure, fracture morphology and the macro-theoretical analysis.
引用
收藏
页码：1290 / 1293
页数：4
相关论文
共 4 条
  • [1] Chen Guodong, 2010, CHEM MACHINERY, V37, P644
  • [2] Failure analysis of a stainless steel pipeline
    Kumar, M. Suresh
    Sujata, M.
    Venkataswamy, M. A.
    Bhaumik, S. K.
    [J]. ENGINEERING FAILURE ANALYSIS, 2008, 15 (05) : 497 - 504
  • [3] Solving some key failure analysis problems using advanced methods for materials testing
    Shipilov, Sergei A.
    [J]. ENGINEERING FAILURE ANALYSIS, 2007, 14 (08) : 1550 - 1573
  • [4] Failure analysis of a hydro-processing reactor
    Wang Yang
    Lu Ye-Bo
    Pan Hong-Liang
    [J]. ENGINEERING FAILURE ANALYSIS, 2009, 16 (01) : 11 - 18
1