Comparison between measured CaO and Al2O3 normalised to CaO-Al2O3 in top slag, calcium aluminate inclusions and results of theoretical calculations

被引:3
作者
Riyahimalayeri, K. [1 ,2 ]
Oelund, P. [1 ]
Selleby, M. [2 ]
机构
[1] Ovako Hofors AB, Mat Res & Dev, SE-81382 Hofors, Sweden
[2] Royal Inst Technol KTH, Dept Mat Sci & Engn, SE-10044 Stockholm, Sweden
关键词
CaO; Al2O3; Top slag; Calcium aluminate; Inclusions; Theoretical calculations; DEOXIDATION EQUILIBRIA; THERMODYNAMIC EVALUATION; MOLTEN IRON; FATIGUE; OXIDE; OPTIMIZATION; STEELS; SYSTEM; MODEL; AL;
D O I
10.1179/1743281212Y.0000000046
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
This study sets out to compare the wt-% CaOslag and Al2O3slag in the binary system of CaO-Al2O3 that were measured in the top slag before teeming, the CaOincl and Al2O3incl in calcium aluminates that were analysed by scanning electron microscopy of the steel samples and the CaOcalc and Al2O3calc that were achieved from theoretical calculations using the total measured elements in the top slag and steel before teeming. The CaOincl and Al2O3incl in all of the calcium aluminate inclusions of this study did not have the same ratio; in the opposite, they covered a large range. The average CaOincl and Al2O3incl in all samples had nearly similar compositions that were close to the border of the phase Ca12Al14O33 in the binary phase diagram of CaO-Al2O3. The CaOslag and Al2O3slag in all samples had almost similar compositions that were close to the border of the phase Ca3Al2O6 in the binary phase diagram of CaO-Al2O3. The results of theoretical calculations were close to the CaOslag and Al2O3slag, but they did not follow the same maximum and minimum tendencies of CaOslag and Al2O3slag.
引用
收藏
页码:369 / 375
页数:7
相关论文
共 30 条
[1]   Gigacycle fatigue properties of 1800 MPa class spring steels [J].
Abe, T ;
Furuya, Y ;
Matsuoka, S .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (02) :159-167
[2]  
[Anonymous], 2010, INCA FEAT SOFTW COMP
[3]   Metallurgy of plastic inclusions to improve fatigue life of engineering steels [J].
Bertrand, C ;
Molinero, J ;
Landa, S ;
Elvira, R ;
Wild, M ;
Barthold, G ;
Valentin, P ;
Schifferl, H .
IRONMAKING & STEELMAKING, 2003, 30 (02) :165-169
[4]   Thermodynamic description of Al2O3-CaO-MnO and Al2O3-FeO-MnO melts -: a model approach [J].
Björkvall, J ;
Du, SC ;
Seetharaman, S .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2000, 24 (03) :353-376
[5]   Ultra-long cycle fatigue of high-strength carbon steels part II: estimation of fatigue limit for failure from internal inclusions [J].
Chapetti, MD ;
Tagawa, T ;
Miyata, T .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :236-244
[6]   PHASE EQUILIBRIUM DIAGRAM OF SYSTEM CAO-AL2O3-CAF2 [J].
CHATTERJEE, AK ;
ZHMOIDIN, GI .
JOURNAL OF MATERIALS SCIENCE, 1972, 7 (01) :93-+
[7]   ASSESSMENT OF CALCIUM-OXYGEN EQUILIBRIUM IN LIQUID-IRON [J].
CHO, SW ;
SUITO, H .
ISIJ INTERNATIONAL, 1994, 34 (03) :265-269
[8]   Thermodynamic Evaluation of Formation of Oxide-Sulfide Duplex Inclusions in Steel [J].
Choudhary, S. K. ;
Ghosh, A. .
ISIJ INTERNATIONAL, 2008, 48 (11) :1552-1559
[9]  
Decterov S.-A., 2004, P 7 INT C MOLT SLAGS, P839
[10]   CRITICAL-EVALUATION AND OPTIMIZATION OF THE THERMODYNAMIC PROPERTIES AND PHASE-DIAGRAMS OF THE MGO-AL2O3, MNO-AL2O3, FEO-AL2O3, NA2O-AL2O3 AND K2O-AL2O3 SYSTEMS [J].
ERIKSSON, G ;
WU, P ;
PELTON, AD .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1993, 17 (02) :189-205