Preparation of Cf/ZrC Composites by Reactive Melt Infiltration at Relatively Low Temperature

被引：0
|
作者：
Zhu Yulin [1 ]
Wang Song [1 ]
Li Wei [1 ]
Chen Zhaohui [1 ]
机构：
[1] Natl Univ Def Technol, Sci & Technol Adv Ceram Fibers & Composites Lab, Changsha 410073, Hunan, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2013年 / 42卷
关键词：
C-f/ZrC composites; reactive melt infiltration; solution-precipitation mechanism; anti-ablation properties; POROSITY; CARBIDE;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
C-f/ZrC composite was prepared by infiltrating porous C-f/C preform with melting Zr2Cu alloy at 1200 degrees C in vacuum. The results show that the ZrC as the main phase has a content of 43.8 +/- 1.3% (volume fraction). The flexural strength and modulus is 105.7 +/- 5.3 MPa and 64.3 +/- 2.8 GPa, respectively. ZrC growth is controlled by solution-precipitation mechanism. The carbon dissolves in the melting metals and forms C-Zr-Cu miscible phase. Then ZrC nanocrystals are deposited after the melt is saturated, and grow quickly by amalgamation and diffusion. The mass loss rate and linear recession rate of the sample is 0.0039 +/- 0.0008 g/s and 0.0023 +/- 0.0012 mm/s, respectively. So the C-f/ZrC composites show good anti-ablation properties.
引用
收藏
页码：447 / 450
页数：4
相关论文
共 12 条
  • [1] Effect of infiltration parameters on composition of W-ZrC composites produced by displacive compensation of porosity (DCP) method
    Adabi, M.
    Amadeh, A.
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2011, 29 (01) : 31 - 37
  • [2] The combined effect of porosity and reactivity of the carbon preforms on the properties of SiC produced by reactive infiltration with liquid Si
    Calderon, N. R.
    Martinez-Escandell, M.
    Narciso, J.
    Rodriguez-Reinoso, F.
    [J]. CARBON, 2009, 47 (09) : 2200 - 2210
  • [3] Hillig W.B., 1998, J AM CERAM SOC, V71, P96
  • [4] Near net-shape/net-dimension ZrC/W-based composites with complex geometries via rapid prototyping and Displacive Compensation of Porosity
    Lipke, David W.
    Zhang, Yunshu
    Liu, Yajun
    Church, Benjamin C.
    Sandhage, Kenneth H.
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2010, 30 (11) : 2265 - 2277
  • [5] The kinetics of incongruent reduction of tungsten carbide via reaction with a hafnium-copper melt
    Liu, Yajun
    Lipke, David W.
    Zhang, Yunshu
    Sandhage, Kenneth H.
    [J]. ACTA MATERIALIA, 2009, 57 (13) : 3924 - 3931
  • [6] ZrC ablation protective coating for carbon/carbon composites
    Sun Wei
    Xiong Xiang
    Huang Bai-yun
    Li Guo-dong
    Zhang Hong-bo
    Chen Zhao-ke
    Zheng Xiang-Lin
    [J]. CARBON, 2009, 47 (14) : 3368 - 3371
  • [7] Fabrication of uniform ZrC coating layer for the coated fuel particle of the very high temperature reactor
    Ueta, Shohei
    Aihara, Jun
    Yasuda, Atsushi
    Ishibashi, Hideharu
    Takayama, Tomoo
    Sawa, Kazuhiro
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2008, 376 (02) : 146 - 151
  • [8] Reaction kinetics and ablation properties of C/C-ZrC composites fabricated by reactive melt infiltration
    Wang, Yiguang
    Zhu, Xiaojuan
    Zhang, Litong
    Cheng, Laifei
    [J]. CERAMICS INTERNATIONAL, 2011, 37 (04) : 1277 - 1283
  • [9] Preparation of ZrB2 based composites by reactive melt infiltration at relative low temperature
    Zhang, Shouming
    Wang, Song
    Li, Wei
    Zhu, Lin
    Chen, Zhaohui
    [J]. MATERIALS LETTERS, 2011, 65 (19-20) : 2910 - 2912
  • [10] Ablation behavior and mechanism of 3D C/ZrC composite in oxyacetylene torch environment
    Zhao, Dan
    Zhang, Changrui
    Hu, Haifeng
    Zhang, Yudi
    [J]. COMPOSITES SCIENCE AND TECHNOLOGY, 2011, 71 (11) : 1392 - 1396
12