Fly Ash Porous Material using Geopolymerization Process for High Temperature Exposure

被引：61

作者：

Abdullah, Mohd Mustafa Al Bakri ^{[1
]}

Jamaludin, Liyana ^{[1
]}

Hussin, Kamarudin ^{[1
]}

Bnhussain, Mohamed ^{[2
]}

Ghazali, Che Mohd Ruzaidi ^{[1
]}

Ahmad, Mohd Izzat ^{[1
]}

机构：

[1] UniMAP, Sch Mat Engn, Kangar 01000, Perlis, Malaysia

[2] KACST, Riyadh 11442, Saudi Arabia

来源：

INTERNATIONAL JOURNAL OF MOLECULAR SCIENCES | 2012年 / 13卷 / 04期

关键词：

geopolymer; pozzolanic material; thermal analysis;

D O I：

10.3390/ijms13044388

中图分类号：

Q5 [生物化学]; Q7 [分子生物学];

学科分类号：

071010 ; 081704 ;

摘要：

This paper presents the results of a study on the effect of temperature on geopolymers manufactured using pozzolanic materials (fly ash). In this paper, we report on our investigation of the performance of porous geopolymers made with fly ash after exposure to temperatures from 600 degrees C up to 1000 degrees C. The research methodology consisted of pozzolanic materials (fly ash) synthesized with a mixture of sodium hydroxide and sodium silicate solution as an alkaline activator. Foaming agent solution was added to geopolymer paste. The geopolymer paste samples were cured at 60 degrees C for one day and the geopolymers samples were sintered from 600 degrees C to 1000 degrees C to evaluate strength loss due to thermal damage. We also studied their phase formation and microstructure. The heated geopolymers samples were tested by compressive strength after three days. The results showed that the porous geopolymers exhibited strength increases after temperature exposure.

引用

页码：4388 / 4395

页数：8

共 22 条

[1] Optimization of Alkaline Activator/fly ASH Ratio on The Compressive Strength of Manufacturing Fly ASH-BASED Geopolymer
Al Bakri, A. M. Mustafa
Kamarudin, H.
Karem, Omar A. K. A.
Ruzaidi, C. M.
Rafiza, A. R.
Norazian, M. N.
[J]. MECHANICAL AND AEROSPACE ENGINEERING, PTS 1-7, 2012, 110-116 : 734 - +
[2] Allahverdi A, 2001, CERAM-SILIKATY, V45, P81
[3] THE ASSESSMENT OF FIRE DAMAGED CONCRETE
CHEW, MYL
[J]. BUILDING AND ENVIRONMENT, 1993, 28 (01) : 97 - 102
[4] GEOPOLYMERS - INORGANIC POLYMERIC NEW MATERIALS
DAVIDOVITS, J
[J]. JOURNAL OF THERMAL ANALYSIS, 1991, 37 (08): : 1633 - 1656
[5] Davidovits J., 1993, CERAMIC T VOL 37, V37, P165
[6] Davidovits J., 1994, Journal Material Education, V16, P91, DOI DOI 10.1016/J.CEMCONCOMP.2009.12.002
[7] Davidovits J., 1994, World Resource Review, V6, P263, DOI DOI 10.1016/J.RSER.2012.07.019
[8] Davidovits J., 1999, GEOPOLYMER INT C P, V11, P9
[9] Davidovits J., 1994, CONCRETE TECHNOLOGY, P383, DOI DOI 10.14359/4523
[10] Davidovits J., 2008, GEOPOLYMER CHEM APPL

← 1 2 3 →