Development of fly ash-based geopolymers using powder sodium silicate activator

被引：13

作者：

Luna-Galiano, Y. ^{[1
]}

Leiva, C. ^{[1
]}

Arroyo, F. ^{[1
]}

Villegas, R. ^{[1
]}

Vilches, L. ^{[1
]}

Fernandez-Pereira, C. ^{[1
]}

机构：

[1] Univ Seville, Chem & Environm Engn Dept, Camino Descubrimientos S-N, Seville 41092, Spain

来源：

MATERIALS LETTERS | 2022年 / 320卷

关键词：

Geopolymers; Fly ash; Degree of reaction; Mercury porosimetry; Compressive strength; Durability tests; DURABILITY;

D O I：

10.1016/j.matlet.2022.132346

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Geopolymer manufacturing by means a ready-mix procedure using powder sodium silicate as activator is described in this paper. Its characteristics are compared with conventional geopolymers using aqueous sodium silicate. Degree of reaction, mercury intrusion porosity and compressive strength were measured at different curing times. Three durability tests were carried out. The geopolymer obtained using powder activator showed slightly lower mechanical properties and better durability results than those found for geopolymers based on aqueous activators. In addition, the manufacture of geopolymers based on powder silicate was easier and simpler than the more common procedure using sodium silicate solutions, so the ready-mix manufacturing could be an alternative to produce geopolymers.

引用

页数：4

共 9 条

[1] Durability of reinforced concrete exposed to aggressive conditions
Aguirre, A. M.
Mejia de Gutierrez, R.
[J]. MATERIALES DE CONSTRUCCION, 2013, 63 (309) : 7 - 38
[2] Resistance of geopolymer materials to acid attack
Bakharev, T
[J]. CEMENT AND CONCRETE RESEARCH, 2005, 35 (04) : 658 - 670
[3] Durability of traditional plasters with respect to blast furnace slag-based plaster
Cerulli, T
Pistolesi, C
Maltese, C
Salvioni, D
[J]. CEMENT AND CONCRETE RESEARCH, 2003, 33 (09) : 1375 - 1383
[4] Quantitative determination of phases in the alkaline activation of fly ash.: Part II:: Degree of reaction
Fernandez-Jimenez, A.
de la Torre, A. G.
Palomo, A.
Lopez-Olmo, G.
Alonso, M. M.
Aranda, M. A. G.
[J]. FUEL, 2006, 85 (14-15) : 1960 - 1969
[5] Contributions to the study of porosity in fly ash-based geopolymers. Relationship between degree of reaction, porosity and compressive strength
Luna-Galiano, Y.
Fernandez-Pereira, C.
Izquierdo, M.
[J]. MATERIALES DE CONSTRUCCION, 2016, 66 (324)
[6] One-part alkali-activated materials: A review
Luukkonen, Tero
Abdollahnejad, Zahra
Yliniemi, Juho
Kinnunen, Paivo
Illikainen, Mirja
[J]. CEMENT AND CONCRETE RESEARCH, 2018, 103 : 21 - 34
[7] Synthesis of heat and ambient cured one-part geopolymer mixes with different grades of sodium silicate
Nematollahi, Behzad
Sanjayan, Jay
Shaikh, Faiz Uddin Ahmed
[J]. CERAMICS INTERNATIONAL, 2015, 41 (04) : 5696 - 5704
[8] A review on alkaline activation: new analytical perspectives
Palomo, A.
Krivenko, P.
Garcia-Lodeiro, I.
Kavalerova, E.
Maltseva, O.
Fernandez-Jimeneza, A.
[J]. MATERIALES DE CONSTRUCCION, 2014, 64 (315)
[9] Ridzuan A. R. M., 2015, Materials Science Forum, V803, P185, DOI 10.4028/www.scientific.net/MSF.803.185

← 1 →