Effects of Different Coatings, Primers, and Additives on Corrosion of Steel Rebars

被引：6
作者：
Afshar, Alireza [1 ]
Jahandari, Soheil [2 ,3 ]
Rasekh, Haleh [4 ]
Rahmani, Aida [2 ,3 ]
Saberian, Mohammad [5 ]
机构：
[1] George Mason Univ, Dept Civil & Environm Engn, Fairfax, VA 22030 USA
[2] Western Sydney Univ, Ctr Infrastructure Engn, Penrith, NSW 2751, Australia
[3] Chem Concrete Pty Ltd, Seven Hills, NSW 2147, Australia
[4] Univ Technol Sydney, Sch Civil & Environm Engn, Sydney, NSW 2007, Australia
[5] RMIT Univ, Sch Engn, Melbourne, Vic 3000, Australia
来源：
POLYMERS | 2023年 / 15卷 / 06期
关键词：
accelerated corrosion; coating systems; rebars; inhibitors; pozzolanic materials; pullout test of steel-concrete bond joints; FLY-ASH; REINFORCED-CONCRETE; SILICA FUME; BOND STRENGTH; MECHANICAL-PROPERTIES; LIGHTWEIGHT CONCRETE; CHLORIDE DIFFUSION; STAINLESS-STEELS; BLENDED CEMENT; BEHAVIOR;
D O I：
10.3390/polym15061422
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
In this research, methods of increasing the corrosion resistance of reinforced concrete were experimentally investigated. The study used silica fume and fly ash at optimized percentages of 10 and 25% by cement weight, polypropylene fibers at a ratio of 2.5% by volume of concrete, and a commercial corrosion inhibitor, 2-dimethylaminoethanol (Ferrogard 901), at 3% by cement weight. The corrosion resistance of three types of reinforcements, mild steel (STt37), AISI 304 stainless steel, and AISI 316 stainless steel, was investigated. The effects of various coatings, including hot-dip galvanizing, alkyd-based primer, zinc-rich epoxy primer, alkyd top coating, polyamide epoxy top coating, polyamide epoxy primer, polyurethane coatings, a double layer of alkyd primer and alkyd top coating, and a double layer of epoxy primer and alkyd top coating, were evaluated on the reinforcement surface. The corrosion rate of the reinforced concrete was determined through results of accelerated corrosion and pullout tests of steel-concrete bond joints and stereographic microscope images. The samples containing pozzolanic materials, the corrosion inhibitor, and a combination of the two showed significant improvement in corrosion resistance by 7.0, 11.4, and 11.9 times, respectively, compared to the control samples. The corrosion rate of mild steel, AISI 304, and AISI 316 decreased by 1.4, 2.4, and 2.9 times, respectively, compared to the control sample; however, the presence of polypropylene fibers reduced the corrosion resistance by 2.4 times compared to the control.
引用
收藏
页数：23
相关论文
共 81 条
[1]   Electrochemistry and surface chemistry of stainless steels in alkaline media simulating concrete pore solutions [J].
Addari, D. ;
Elsener, B. ;
Rossi, A. .
ELECTROCHIMICA ACTA, 2008, 53 (27) :8078-8086
[2]   Corrosion resistance evaluation of rebars with various primers and coatings in concrete modified with different additives [J].
Afshar, Alireza ;
Jahandari, Soheil ;
Rasekh, Haleh ;
Shariati, Mahdi ;
Afshar, Abdollah ;
Shokrgozar, Ali .
CONSTRUCTION AND BUILDING MATERIALS, 2020, 262
[3]   Reinforcement corrosion in concrete structures, its monitoring and service life prediction - a review [J].
Ahmad, S .
CEMENT & CONCRETE COMPOSITES, 2003, 25 (4-5) :459-471
[4]   Bond analysis of corroded reinforced concrete beams under monotonic and fatigue loads [J].
Al-Hammoud, Rania ;
Soudki, Khaled ;
Topper, Timothy H. .
CEMENT & CONCRETE COMPOSITES, 2010, 32 (03) :194-203
[5]   Performance of generic and proprietary corrosion inhibitors in chloride-contaminated silica fume cement concrete [J].
Al-Mehthel, Mohamed ;
Al-Dulaijan, Salah ;
Al-Idi, Saleh H. ;
Shameem, Mohammed ;
Ali, M. R. ;
Maslehuddin, Mohammed .
CONSTRUCTION AND BUILDING MATERIALS, 2009, 23 (05) :1768-1774
[6]  
[Anonymous], 1998, 129445 EN ISO
[7]  
[Anonymous], 2003, G4499 ASTM INT
[8]  
[Anonymous], 1998, D4541 ASTM
[9]  
Auyeung Y, 2000, ACI MATER J, V97, P214
[10]  
AzariJafari H., 2015, SPEC PUBL J L B SMIT, V302, P416
123456789