Effect of Cavitation Water Jet Peening on Properties of AlCoCrFeNi High-Entropy Alloy Coating

被引：1

作者：

Wu, Rui ^{[1
]}

Yang, Yongfei ^{[1
]}

Shi, Weidong ^{[1
]}

Cao, Yupeng ^{[1
]}

Liu, Yu ^{[1
]}

Zhang, Jinchao ^{[1
]}

机构：

[1] Nantong Univ, Sch Mech Engn, Nantong 226019, Peoples R China

来源：

COATINGS | 2023年 / 13卷 / 11期

关键词：

cavitation water jet peening; high-entropy alloy coating; microstructural evolution; COMPRESSIVE RESIDUAL-STRESS; FATIGUE-CRACK GROWTH; STAINLESS-STEEL; DURALUMIN PLATE; STRENGTH; IMPROVEMENT;

D O I：

10.3390/coatings13111972

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High-entropy alloys have been widely used in engineering manufacturing due to their hardness, good wear resistance, excellent corrosion resistance, and high-temperature oxidation resistance. However, it is inevitable that metallurgical defects, such as micro cracks and micro pores, are produced when preparing the coating, which affects the overall performance of the alloy to a certain extent. In view of this situation, cavitation water jet peening (CWJP) was used to strengthen the AlCoCrFeNi high-entropy alloy coating. The effect of CWJP impact time on the microstructure and mechanical properties of CWJP were investigated. The results show that CWJP can form an effective hardening layer on the surface layer of the AlCoCrFeNi high-entropy alloy. When the CWJP impact time was 4 h, the microhardness of the surface layer of the specimen was harder than that of 2 h and 6 h, and the CWJP impact time had little effect on the thickness of the hardening layer. Observing the surface of the untreated and CWJP-treated specimens using the EBSD test, it was evident that the microstructure was significantly homogenized, the grains were refined, and the proportion of small-angle grain boundaries increased. The system reveals the grain refinement mechanism of the AlCoCrFeNi high-entropy alloy coating during plastic deformation. This study aims to provide a new surface strengthening method for obtaining high-performance AlCoCrFeNi high-entropy alloy coatings.

引用

页数：15

共 25 条

[1] A study on the compressive residual stress due to waterjet cavitation peening [J].

Balamurugan, K. ;

Uthayakumar, M. ;

Gowthaman, S. ;

Pandurangan, R. .

ENGINEERING FAILURE ANALYSIS, 2018, 92 :268-277

[2] Investigation on fatigue crack growth behaviour in S45C steel by water cavitation peening with aeration [J].

Han, B. ;

Ju, D. Y. ;

Nemoto, T. .

PRICM 6: SIXTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-3, 2007, 561-565 :2485-+

[3] Investigation of water cavitation peening-induced microstructures and residual stress in the near-surface spring steel SAE 1070 [J].

Han, B. ;

Zhang, H. ;

Ju, D. Y. .

MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 :1036-+

[4] A Method for Improving Compressive Residual Stress of Small Holes Surface by Water-jet Cavitation Peening [J].

Han, B. ;

Ju, D. Y. .

ADVANCED MATERIALS SCIENCE AND TECHNOLOGY, 2009, 614 :137-142

[5] Improvement of residual stress in gear using water peening by a cavitation jet technique [J].

Ju, DY ;

Uchiyama, T ;

Machida, H ;

Kanawa, T ;

Oba, R ;

Sunayama, Y ;

Tsuda, H .

ECRS 6: PROCEEDINGS OF THE 6TH EUROPEAN CONFERENCE ON RESIDUAL STRESSES, 2002, 404-7 :635-640

[6]

Kohl R.E., 1968, Mining

[7]

LI L Q, 2019, China Laser, V46, P174

[8]

Li X., 2016, Hot Work. Process, V45, P19

[9]

Li Z., 2007, Modern Surface Engineering Technology, P444

[10] An assessment on the future development of high-entropy alloys: Summary from a recent workshop [J].

Lu, Z. P. ;

Wang, H. ;

Chen, M. W. ;

Baker, I. ;

Yeh, J. W. ;

Liu, C. T. ;

Nieh, T. G. .

INTERMETALLICS, 2015, 66 :67-76

← 1 2 3 →