Investigation of structural, dielectric and ferroelectric properties of nickel substituted BST ceramics

The current study demonstrates the effect of Ni-substitution on the structural, dielectric and ferroelectric properties of Ba0.90Sr0.10Ti1-xNixO3 (where x = 0.000, 0.005, 0.015 and 0.025) ceramics, synthesized by solid-state reaction approach. A pure perovskite phase with tetragonal structure has been confirmed by X-ray diffraction (XRD) analysis. Scanning electron microscope (SEM) images revealed change in microstructure. The dielectric behavior of the prepared ceramics was investigated as a function of temperature (30-150 degrees C) at different frequencies. The results indicate that there is an increase in dielectric constant (epsilon RT) and low dielectric loss (tan delta RT) were obtained at room temperature by substitution of Ni2+ ions in BST ceramics, offering a promising material for capacitor applications at room temperature. Room temperature P-E loops were recorded at different applied electric fields and typical hysteresis loops were obtained. Improvement in the values of Pr and Pmax was observed by substitution of Ni2+ ions.