Improvement of Critical Intergranular Fracture Stress by Increasing Carbon Content in Tempered Martensite Steels

被引:0
作者
Yoshimura, Masahide [1 ]
Hoshino, Manabu [1 ]
Fujioka, Masaaki [1 ]
机构
[1] Nippon Steel Corp Ltd, Steel Res Labs, Res & Dev, 20-1 Shintomi, Futtsu, Chiba 2938511, Japan
关键词
intergranular fracture; martensite; segregation; substructure; grain size; GRAIN-BOUNDARY SEGREGATION; TRANSITION-TEMPERATURE; FE-P; PHOSPHORUS; EMBRITTLEMENT; TOUGHNESS; STRENGTH; ELEMENTS;
D O I
10.2355/isijinternational.ISIJINT-2023-268
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Effect of carbon (C) content (0.05 mass% to 0.3 mass%) on critical intergranular fracture stress of tempered martensite steel was investigated using 3 mass% manganese (Mn) steel. The critical intergranular fracture stress was obtained by calculating the maximum principal stress at fracture in a tensile test of circumferentially notched round bar specimen using elastoplastic finite element analysis. As a result, critical intergranular fracture stress of tempered martensite steel increased with increasing the C content. Therefore, the dominant factors of critical intergranular fracture stress were examined from the viewpoints of the amount of segregation of each element on prior-austenite grain boundaries and the grain size of the martensite substructure. The first result was found to be the effect of reducing the amount of Mn segregation by increasing the C content. This was thought to be because cementite acts as a solid solution site for Mn, and the amount of Mn in solid solution in the matrix phase is reduced by increasing the C content. The second result was found to be the effect of refining the substructure of martensite surrounded by high angle grain boundaries by increasing the C content. This indicates that grain size also affects crack initiation resistance in intergranular fracture by determining the stress concentration at the grain boundaries as the distance of dislocation accumulation.
引用
收藏
页码:401 / 411
页数:11
相关论文
共 24 条
[11]  
Mclean D., 1957, Grain Boundaries in Metal, P116
[12]  
McMahon C.J., 1989, MAT SCI FORUM, V46, P61, DOI [10.4028/www.scientific.net/MSF.46.61, DOI 10.4028/WWW.SCIENTIFIC.NET/MSF.46.61]
[13]   The morphology and crystallography of lath martensite in Fe-C alloys [J].
Morito, S ;
Tanaka, H ;
Konishi, R ;
Furuhara, T ;
Maki, T .
ACTA MATERIALIA, 2003, 51 (06) :1789-1799
[14]   TEMPER EMBRITTLEMENT OF NI-CR STEELS BY PHOSPHORUS [J].
MULFORD, RA ;
MCMAHON, CJ ;
POPE, DP ;
FENG, HC .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (08) :1183-1195
[15]   Intergranular fracture stress and phosphorus grain boundary segregation of a Mn-Ni-Mo steel [J].
Naudin, C ;
Frund, JM ;
Pineau, A .
SCRIPTA MATERIALIA, 1999, 40 (09) :1013-1019
[16]   THE INFLUENCE OF GRAIN-BOUNDARY CARBIDE AND GRAIN-SIZE ON THE CLEAVAGE STRENGTH AND IMPACT TRANSITION-TEMPERATURE OF STEEL [J].
PETCH, NJ .
ACTA METALLURGICA, 1986, 34 (07) :1387-1393
[17]  
PREECE A, 1953, J IRON STEEL I, V173, P387
[18]  
SUZUKI S, 1985, T IRON STEEL I JPN, V25, P62
[19]   EFFECT OF CARBON ON THE GRAIN-BOUNDARY SEGREGATION OF PHOSPHORUS IN ALPHA-IRON [J].
SUZUKI, S ;
OBATA, M ;
ABIKO, K ;
KIMURA, H .
SCRIPTA METALLURGICA, 1983, 17 (11) :1325-1328
[20]   THE CALCULATION OF TRANSITION-TEMPERATURE CHANGES IN STEELS DUE TO TEMPER EMBRITTLEMENT [J].
TAKAYAMA, S ;
OGURA, T ;
FU, SC ;
MCMAHON, CJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1980, 11 (09) :1513-1530