Effects of Heat-Treatment and Cold-Rolling on Mechanical Properties and Impact Failure Resistance of New Al 6082 Aluminum Alloy by Continuous Casting Direct Rolling Process

Al 6082 aluminum alloy has excellent corrosion resistance, strength, and formability. However, owing to the recrystallization effect of a hot working process, coarse grains form easily in this material, which reduces its strength and service life. The novel continuous casting direct rolling (CCDR) method can prevent the deterioration of this material. Thus, we used CCDR Al 6082 aluminum alloy as the research material in this study. By subjecting a CCDR Al 6082 aluminum alloy to heat treatment (T4 and T6) and cold rolling, the influence of recrystallization effect on its mechanical properties and on impact failure resistance were explored. The results demonstrated that the specimen subjected to T4 heat treatment had a higher elongation and that the specimen subjected to T6 heat treatment had a higher strength. After cold rolling, the hardness and strength of the specimens subjected to different heat treatments (coded T4R4 and T6R4) increased because of the work's hardening effect. Moreover, the elongations of both specimens decreased, but they were higher than the industrial standard (>10%). The strength of specimen T6R4 was higher (up to 400 MPa) than specimen T4R4. Moreover, relative to specimen T4R4, specimen T6R4 had greater tensile and Charpy impact failure toughness.