Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water

被引:4
作者
Qiao, Yufei [1 ,2 ]
Zheng, Hui [3 ]
Tan, Jibo [1 ]
Yang, Shuangliang [3 ]
Zhang, Ziyu [1 ]
Li, Jie [3 ]
Wu, Xinqiang [1 ]
Ke, Wei [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
[3] State Nucl Power Plant Serv Co, Shanghai 200233, Peoples R China
关键词
Stainless steel; Thermal aging; Corrosion fatigue; Ferrite; High temperature corrosion; ENVIRONMENTALLY ASSISTED CRACKING; CORROSION-FATIGUE; DELTA-FERRITE; MECHANICAL-PROPERTIES; FRACTURE-TOUGHNESS; G-PHASE; EMBRITTLEMENT; INITIATION; WELD; CF3;
D O I
10.1016/j.corsci.2024.111869
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effect of thermal aging (0 h- 15,000 h at 400 degrees C) on the low cycle fatigue properties of Z3CN20.09M stainless steel was investigated. The micro-hardness of the ferrite increases with thermal aging time, while that of the austenite is almost unchanged. The fatigue life of Z3CN20.09M stainless steel in high-temperature pressurized water decreases with thermal aging time. The fatigue cracks formed everywhere, mainly including at slip bands in austenite, at the delta/gamma phase boundary and in ferrite. Thermal aging promotes crack initiation and propagation in ferrite. The effect of thermal aging on the fatigue damage process is discussed.
引用
收藏
页数:13
相关论文
共 50 条
[41]   SCC behaviours of austenitic stainless steel Z3CN20-09M in high temperature water [J].
Lu, Y. H. ;
Chen, Z. R. ;
Zhu, X. F. ;
Shoji, T. .
MATERIALS SCIENCE AND TECHNOLOGY, 2014, 30 (15) :1944-1950
[42]   Effect of Sigma Phases on Moderate-Temperature Tensile Properties of Z3CN20.09M CASS Used for Primary Coolant Pipe of Nuclear Power Plant [J].
Wang, Yongqiang ;
Hu, Chaojun ;
Li, Na ;
Lin, Suhua ;
Ge, Zhangqi ;
Zheng, Chengsi .
COATINGS, 2023, 13 (01)
[43]   Strain-rate dependent fatigue behavior of 316LN stainless steel in high-temperature water [J].
Tan, Jibo ;
Wu, Xinqiang ;
Han, En-Hou ;
Ke, Wei ;
Wang, Xiang ;
Sun, Haitao .
JOURNAL OF NUCLEAR MATERIALS, 2017, 489 :33-41
[44]   Effect of thermal aging on oxide film of stainless steel weld overlay cladding exposed to high temperature water [J].
Cao, Xinyuan ;
Zhu, Ping ;
Wang, Wei ;
Liu, Tingguang ;
Lu, Yonghao ;
Shoji, Tetsuo .
MATERIALS CHARACTERIZATION, 2018, 138 :195-207
[45]   Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment [J].
Xi, Kai ;
Qi, Wenlong ;
Li, Yuanfei ;
Zhao, Yang ;
Liu, Xiangbing ;
Zhang, Tao ;
Wang, Fuhui .
MATERIALS CHARACTERIZATION, 2024, 217
[46]   Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment [J].
Wu, Huanchun ;
Liu, Xiangbing ;
Xu, Chaoliang ;
Li, Yuanfei ;
Yin, Jian ;
Jin, Xiao ;
Jia, Wenqing ;
Qian, Wangjie ;
Wang, Peng ;
Zhang, Yanwei .
METALS, 2024, 14 (05)
[47]   EFFECTS OF THERMAL AGING ON MICRO-MECHANICAL PROPERTIES AND IMPACT FRACTURE BEHAVIOR OF Z3CN20-09M STAINLESS STEELS [J].
Li Shilei ;
Wang Xitao ;
Wang Yanli ;
Li Shuxiao .
ACTA METALLURGICA SINICA, 2011, 47 (06) :751-756
[48]   Effects of thermal aging on the stress corrosion cracking behavior of cast stainless steel with different d-ferrite levels in high temperature water environment [J].
Lu, Wen-Feng ;
Huang, Jiunn-Yuan ;
Yung, Tung-Yuan ;
Chen, Tai-Cheng ;
Tsai, Kun-Chao .
JOURNAL OF NUCLEAR MATERIALS, 2022, 568
[49]   THE MICROSTRUCTURE AND TENSILE FRACTURE BEHAVIOR OF LONG TERM THERMAL AGED Z3CN20-09M STAINLESS STEEL [J].
Zheng Kai ;
Wang Yanli ;
Li Shilei ;
Lu Xuming ;
Wang Xitao ;
Xue Fei .
ACTA METALLURGICA SINICA, 2013, 49 (02) :175-180
[50]   Influence of Thermal Aging on Tensile and Low Cycle Fatigue Behavior of Type 316LN Austenitic Stainless Steel Weld Joint [J].
Kumar, T. Suresh ;
Nagesha, A. ;
Kumar, J. Ganesh ;
Parameswaran, P. ;
Sandhya, R. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (08) :3257-3273