Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water

被引：3
|
作者：
Qiao, Yufei [1 ,2 ]
Zheng, Hui [3 ]
Tan, Jibo [1 ]
Yang, Shuangliang [3 ]
Zhang, Ziyu [1 ]
Li, Jie [3 ]
Wu, Xinqiang [1 ]
Ke, Wei [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
[3] State Nucl Power Plant Serv Co, Shanghai 200233, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 229卷
关键词：
Stainless steel; Thermal aging; Corrosion fatigue; Ferrite; High temperature corrosion; ENVIRONMENTALLY ASSISTED CRACKING; CORROSION-FATIGUE; DELTA-FERRITE; MECHANICAL-PROPERTIES; FRACTURE-TOUGHNESS; G-PHASE; EMBRITTLEMENT; INITIATION; WELD; CF3;
D O I：
10.1016/j.corsci.2024.111869
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of thermal aging (0 h- 15,000 h at 400 degrees C) on the low cycle fatigue properties of Z3CN20.09M stainless steel was investigated. The micro-hardness of the ferrite increases with thermal aging time, while that of the austenite is almost unchanged. The fatigue life of Z3CN20.09M stainless steel in high-temperature pressurized water decreases with thermal aging time. The fatigue cracks formed everywhere, mainly including at slip bands in austenite, at the delta/gamma phase boundary and in ferrite. Thermal aging promotes crack initiation and propagation in ferrite. The effect of thermal aging on the fatigue damage process is discussed.
引用
收藏
页数：13
相关论文
共 50 条
  • [21] Passive film properties of Z3CN20.09M duplex stainless steel aged for different times
    You, Ye
    Chen, Yuefeng
    Yang, Bin
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2018, 69 (09): : 1205 - 1217
  • [22] Effect of sigma phase precipitation on the mechanical and wear properties of Z3CN20.09M cast duplex stainless steel
    Wang, Y. Q.
    Han, J.
    Wu, H. C.
    Yang, B.
    Wang, X. T.
    NUCLEAR ENGINEERING AND DESIGN, 2013, 259 : 1 - 7
  • [23] Pitting behavior of thermally aged Z3CN20.09M cast stainless steel for primary coolant pipe of nuclear power plant
    Chen, Yuefeng
    Chen, Bo
    Dong, Fang
    Yang, Bin
    Li, Shilei
    Yu, Xiaoyi
    ENGINEERING FAILURE ANALYSIS, 2018, 83 : 1 - 8
  • [24] Mechanical properties and eddy current testing of thermally aged Z3CN20.09M cast duplex stainless steel
    Liu, Tonghua
    Wang, Wei
    Qiang, Wenjiang
    Shu, Guogang
    JOURNAL OF NUCLEAR MATERIALS, 2018, 501 : 1 - 7
  • [25] Effect of multiple heat treatments on fracture property of centrifugal casting stainless steels Z3CN20.09M with long-term thermal aging degradation
    Fan, Min-yu
    Jia, Wen-qing
    Yu, Wei-wei
    Wang, Dong-ying
    Guan, Meng
    Cao, Yu
    Xue, Fei
    Liu, Yin-li
    Yao, Jing-wen
    Lin, Bin
    Yu, Ting
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2021, 28 (02) : 223 - 231
  • [26] Effect of multiple heat treatments on fracture property of centrifugal casting stainless steels Z3CN20.09M with long-term thermal aging degradation
    Min-yu Fan
    Wen-qing Jia
    Wei-wei Yu
    Dong-ying Wang
    Meng Guan
    Yu Cao
    Fei Xue
    Yin-li Liu
    Jing-wen Yao
    Bin Lin
    Ting Yu
    Journal of Iron and Steel Research International, 2021, 28 : 223 - 231
  • [27] Effect of long-term aging on the fracture toughness of primary coolant piping material Z3CN20.09M
    Yu, Weiwei
    Fan, Minyu
    Gao, Hongbo
    Yu, Dunji
    Xue, Fei
    Chen, Xu
    NUCLEAR ENGINEERING AND DESIGN, 2018, 327 : 150 - 160
  • [28] EFFECT OF CREVICE ON LOW-CYCLE FATIGUE BEHAVIOR OF PRESSURE-VESSEL STEEL IN HIGH-TEMPERATURE PRESSURIZED-WATER
    SATO, S
    KATADA, Y
    NAGATA, N
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1995, 81 (08): : 827 - 832
  • [29] EFFECT OF SIGMA PHASE PRECIPITATION ON THE MECHANICAL PROPERTIES OF Z3CN20.09M STAINLESS STEEL USED FOR PRIMARY COOLANT PIPES OF NUCLEAR POWER PLANT
    Yang, Bin
    Wang, Yongqiang
    Han, Jun
    Wu, Huanchun
    PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON MECHANICS AND MATERIALS IN DESIGN (M2D2017), 2017, : 1861 - 1862
  • [30] Effects of of temperature on corrosion fatigue behavior of 316LN stainless steel in high-temperature pressurized water
    Zhang, Ziyu
    Tan, Jibo
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    Rao, Jiancun
    CORROSION SCIENCE, 2019, 146 (80-89) : 80 - 89
12345