Rosmarinus officinalis extract as eco-friendly corrosion inhibitor for copper in 1 M nitric acid solution: Experimental and theoretical studies

Rosmarinus officinalis extract (ROE) was studied chemically (mass loss, ML), electrochemically impedance spectrometry (EIS), and potentiodynamic polarization (PDP) as a corrosion inhibitor in 1 M nitric acid. According to ML, ROE is effective like a copper preservative in 1 M HNO3 acid solution at R.T by improving inhibitor concentration up to 77 % at 300 ppm and 25 degrees C. A study was conducted regarding the effect of temperature on copper adsorption, as well as the calculation of adsorption coefficients. Results indicated that physisorption increases with temperature, indicating a decrease in inhibition efficiency (%IE). Langmuir's adsorption model was consistent with the adsorption mechanism. Using the PDP method, the inhibitor accumulated on the copper surface in mixed forms. Moreover, EIS revealed that the value of double-layer capacitance dropped with an increased dose of ROE, while the charge transfer resistance improved. A different approach was taken to the examination of surfaces. Both theoretical studies and practical results were calculated and compared to demonstrate that the results were valid.(c) 2022 The Author(s). Published by Elsevier B.V. on behalf of King Saud University. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).