Combination of Digital Image Correlation (DIC) and in situ 3D-μ-CT in the analysis of the relationship between strains and porosity under creep loading

被引：0

作者：

Camin, B. ^{[1
]}

Hornig-Klamroth, J. ^{[2
]}

zu Bentheim, N. ^{[2
]}

机构：

[1] Hsch Bremerhaven, Fachbereich Technol 1, Fachgebiet Werkstofftechn, Karlstadt 8, D-27568 Bremerhaven, Germany

[2] Berliner Hsch Tech, Fachbereich 8, Luxemburger Str 10, D-13353 Berlin, Germany

来源：

PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2023年 / 60卷 / 02期

关键词：

Digital Image Correlation; X-ray-CT; Synchrotron; Creep; Porosity; DAMAGE; TOMOGRAPHY;

D O I：

10.1515/pm-2023-0008

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In situ 3D mu-XCT allows the time and space resolved measurement and analysis of material damage in the component volume, whereas the Digital Image Correlation (DIC) is a 2D method for the analysis of deformation measured on the surfaces of components. In situ 3D mu-XCT measurements were performed on cylindrical specimen made of SiC particle reinforced titanium MMC (MMC: Metal Matrix Composite) (15 % SiC particles) during creep load. The formation and evolution of voids were subsequently analyzed. Due to the rotationally symmetric sample geometry, the analysis of the deformation in the interior of the material by DIC using 2D slices is possible and evident. The dot pattern required to calculate the strain using DIC (speckle pattern) is provided by the intrinsic particle reinforcement of the MMCs. Temporally and locally changing and time-variant strain fields in both the tensile as well as the compressive range could be detected correlating with void formation and development area.

引用

页码：93 / 107

页数：15

共 26 条

[11] Characterization of Polycrystalline Materials Using Synchrotron X-ray Imaging and Diffraction Techniques
Ludwig, W.
King, A.
Herbig, M.
Reischig, P.
Marrow, J.
Babout, L.
Lauridsen, E. M.
Proudhon, H.
Buffiere, J. Y.
[J]. JOM, 2010, 62 (12) : 22 - 28
[12] Study of the interaction of a short fatigue crack with grain boundaries in a cast Al alloy using X-ray microtomography
Ludwig, W
Buffière, JY
Savelli, S
Cloetens, P
[J]. ACTA MATERIALIA, 2003, 51 (03) : 585 - 598
[13] On strain and damage interactions during tearing: 3D in situ measurements and simulations for a ductile alloy (AA2139-T3)
Morgeneyer, Thilo F.
Taillandier-Thomas, Thibault
Buljac, Ante
Helfen, Lukas
Hild, Francois
[J]. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2016, 96 : 550 - 571
[14] Layout and first results of the nanotomography endstation at the P05 beamline at PETRA III
Ogurreck, M.
Greving, I.
Marschall, F.
Vogt, H.
Last, A.
do Rosario, J. J.
Leib, E. W.
Beckmann, F.
Wilde, F.
Mueller, M.
[J]. XRM 2014: PROCEEDINGS OF THE 12TH INTERNATIONAL CONFERENCE ON X-RAY MICROSCOPY, 2016, 1696
[15] A Simplified Procedure to Determine Post-necking True Stress-Strain Curve from Uniaxial Tensile Test of Round Metallic Specimen Using DIC
Paul, Surajit Kumar
Roy, Satish
Sivaprasad, S.
Tarafder, S.
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (09) : 4893 - 4899
[16] DIGITAL IMAGING TECHNIQUES IN EXPERIMENTAL STRESS-ANALYSIS
PETERS, WH
RANSON, WF
[J]. OPTICAL ENGINEERING, 1982, 21 (03) : 427 - 431
[17] Pineau A., 2007, FAILURE OF METALS, P684
[18] The use of nano-computed tomography (nano-CT) in non-destructive testing of metallic parts made by laser powder-bed fusion additive manufacturing
Salarian, Mehrnaz
Toyserkani, Ehsan
[J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 98 (9-12) : 3147 - 3153
[19] In situ tomographic investigation of damage development in ± 45° carbon fibre reinforced laminates
Sket, F.
Rodriguez-Hortala, M.
Molina-Aldareguia, J. M.
Llorca, J.
Maire, E.
Requena, G.
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (05) : 587 - 593
[20] APPLICATION OF AN OPTIMIZED DIGITAL CORRELATION METHOD TO PLANAR DEFORMATION ANALYSIS
SUTTON, MA
CHENG, MQ
PETERS, WH
CHAO, YJ
MCNEILL, SR
[J]. IMAGE AND VISION COMPUTING, 1986, 4 (03) : 143 - 150

← 1 2 3 →