Microstructures evolution and chloride migration characteristics of concrete under ultra-deep underground environment

被引：40
作者：
Chen, Yong-qing [1 ,2 ,3 ]
Ma, Xiong-ying [1 ,2 ,3 ]
Tong, Xin-yang [1 ,2 ,3 ]
Kang, Xin [1 ,2 ,3 ]
机构：
[1] Hunan Univ, Key Lab Bldg Safety & Energy Efficiency, Minist Educ, Changsha 410082, Peoples R China
[2] Hunan Univ, Natl Ctr Int Res Collaborat Bldg Safety & Environm, Changsha 410082, Peoples R China
[3] Hunan Univ, Coll Civil Engn, Changsha 410082, Peoples R China
来源：
CEMENT & CONCRETE COMPOSITES | 2023年 / 137卷
关键词：
Ultra-deep buried concrete; Ca leaching; Micro-nano pores; Cracks propagation; Chloride attack; Bound chloride; CEMENT-BASED MATERIALS; C-S-H; DC STRAY CURRENT; BOUND CHLORIDE; BINDING; MECHANISMS; CORROSION; INCREASE; CRACKING; MODULUS;
D O I：
10.1016/j.cemconcomp.2023.104936
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Understanding the microstructures evolution and chloride migration characteristics of concrete is essential to solve the durability problem of reinforced concrete structures in ultra-deep buried rail transit projects (40 m-100 m). Herein, we developed a novel experimental system that can simulate the corrosion process under high hydraulic pressure and stray current coexistence environment. The changes in microstructures, phases, elements, minerals, and the Ca-leaching were comprehensively investigated. Further, the mechanisms of pores and cracks propagation, and migration characteristics of chloride ions were revealed. The results showed that stray current and hydraulic pressure significantly altered the microstructures of concrete, both of which led to the increase of specific surface area, porosity, pore diameter and more ink-bottle-shaped pores. The development of dominant microfractures and three types of crack propagation patterns caused by hydraulic pressure were found, and the mechanical framework for "local fracturing" was established. Migration characteristics in micro-nano scale showed chloride ions were mainly transported along the pores, and the decrease of adsorption sites was the main reason.
引用
收藏
页数：21
相关论文
共 61 条
[21]   The influence of water removal techniques on the composition and microstructure of hardened cement pastes [J].
Collier, N. C. ;
Sharp, J. H. ;
Milestone, N. B. ;
Hill, J. ;
Godfrey, I. H. .
CEMENT AND CONCRETE RESEARCH, 2008, 38 (06) :737-744
[22]   The influence of DC stray current on pipeline corrosion [J].
Cui, Gan ;
Li, Zi-Li ;
Yang, Chao ;
Wang, Meng .
PETROLEUM SCIENCE, 2016, 13 (01) :135-145
[23]   Effect of cracks on concrete diffusivity: A meso-scale numerical study [J].
Du, Xiuli ;
Jin, Liu ;
Zhang, Renbo ;
Li, Yue .
OCEAN ENGINEERING, 2015, 108 :539-551
[24]   Chloride diffusivity in saturated cement paste subjected to external mechanical loadings [J].
Du, Xiuli ;
Jin, Liu ;
Zhang, Renbo .
OCEAN ENGINEERING, 2015, 95 :1-10
[25]  
Dubinin MI., 1975, Progress in surface and membrane science, P1
[26]  
Erdogan F., 1963, J Basic Eng, V85, P519, DOI [10.1115/1.3656897, DOI 10.1115/1.3656897]
[27]   Effect of drying on cement-based materials pore structure as identified by mercury intrusion porosimetry -: A comparative study between oven-, vacuum-, and freeze-drying [J].
Gallé, C .
CEMENT AND CONCRETE RESEARCH, 2001, 31 (10) :1467-1477
[28]  
Gregg S.J., 1967, J Electrochem Soc, DOI [10.1149/1.2426447, DOI 10.1149/1.2426447]
[29]  
Griffith AA, 1921, Phil. Trans. R. Soc. A., V221
[30]   Effect of bound chloride on extraction of water soluble chloride in cement-based materials exposed to a chloride salt solution [J].
He, Fuqiang ;
Wang, Ruipan ;
Shi, Caijun ;
Zhang, Runxiao ;
Shi, Zhenguo ;
Zhang, Duo .
CONSTRUCTION AND BUILDING MATERIALS, 2018, 160 :223-232
1234567