Investigating the impact of electron beam irradiation on electrical, magnetic, and optical properties of XLPE/Co3O4 nanocomposites

Nowadays, many researchers aim to fill polymer materials with inorganic nanoparticles to enhance the polymer properties and gain the merits of the polymeric host matrix. Sol-gel synthesized Co3O4 nanoparticles are subjected to different doses of electron beam (10, 20, and 30 kGy) to study their physiochemical properties and choose the optimized nanoparticles to fill our polymeric matrix. Crosslinked polyethylene (XLPE) has been filled with 5 wt % of un-irradiated cobalt oxide nanoparticles using the melt extruder method. The structural, optical, magnetic, and electrical properties of the XLPE/Co3O4 nanocomposite before and after exposure to different doses of electron beam radiation have been characterized. The crystallite size of face-centered cubic spinel Co3O4 nanoparticles has been confirmed by XRD whereas and their unique truncated octahedral shape obviously appears in SEM micrographs. The crystallite size of Co3O4 nanoparticles has decreased from 47.5 to 31.5 nm upon irradiation at a dose of 30 kGy, and significantly decreased to 18.5 nm upon filling inside XLPE matrix. Related to the oxidation effect of the electron beam, the Co2+/Co3+ ratio on the surface of Co3O4 nanoparticles has decreased upon irradiation as verified by XPS technique. This consequently caused the partial elimination of oxygen vacancies, mainly responsible for the weak ferromagnetic behavior of Co3O4 in its nanoscale. This appears as decreased saturation magnetization as depicted by VSM. The XLPE/Co3O4 nanocomposite has also shown weak ferromagnetic behavior but the coercive field (Hc) has increased from 112.57 to 175.72 G upon filling inside XLPE matrix and decreased to 135.18 G after irradiating the nanocomposite at a dose of 30 kGy. The ionic conductivity of XLPE has increased from 0.133 x 10(-7) to 2.198 x 10(-3) S/cm upon filling with Co3O4 nanoparticles while a slight increase is observed upon irradiation.